Abstract:Nanocrystalline Ti1- x Crx O2 (0 ≤ x ≤ 0.20) samples were synthesised via acid-modified sol-gel process and characterised with various techniques, such as HRTEM, FESEM, Raman, XPS, DTA and VSM. The TEM image of TiO2 exhibits elongated nanoparticles with an average size of 10 nm. The HRTEM in combination with selected area electron diffraction (SAED) reveals the interplanar spacing and polycrystalline nature of the samples, respectively. FESEM micrographs divulge nonuniform morphologies and less aggregation of the particles in the doped sample. Raman spectra ensure the phase purity of the samples and a blue shift on Cr doping. X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. Room temperature magnetic measurements exhibit a significant variation in the magnetic parameters on Cr doping in TiO2 . The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance is studied for the degradation of methylene blue (MB) dye under visible light irradiation. A higher photocatalytic efficiency is found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment. LAY DESCRIPTION: In the present study, nanoparticles of TiO2 and Cr-doped TiO2 have been synthesised by a cost-effective acid-modified sol-gel process. The effect of Cr doping on the microstructure, thermal, magnetic and photocatalytic properties of TiO2 were explored in detail. The transmission electron microscopy (TEM) images exhibit the presence of elongated nanoparticles with an average size of 10 nm. Field emission scanning electron microscopy (FESEM) was used to study the surface morphology of the synthesised materials, which revealed nonuniform morphologies and less aggregation of the particles in the Cr-doped sample. Energy dispersive x-ray spectroscopy (EDS) confirms the elemental compositions with the appropriate stoichiometry of the elements. Raman spectra ensure the phase purity of the materials and also a blue shift with the incorporation of Cr ions in TiO2 . X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. The magnetic nature of all the synthesised samples was examined through the vibrating sample magnetometer (VSM) and revealed weak ferromagnetic behaviour of the samples. These results signify that the oxygen vacancies and defects play a crucial role in developing the ferromagnetic nature of oxide semiconductors. The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance of the prepared samples was studied for the degradation of methylene blue (MB) dye under irradiation of visible light. A higher photocatalytic efficiency was found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment.

Comparison of Cr and Sr doping into TiO 2 for photocatalytic removal of gaseous 1,2 dichloroethane

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

A H2O2 Oxidation Approach to Ti3C2/TiO2 for Efficient Photocatalytic Removal of Distinct Organic Pollutants in Water.

Tricrystalline TiO2 with Enhanced Photocatalytic Activity and Durability for Removing Volatile Organic Compounds from Indoor Air

Transition Metal Doping Effect and High Catalytic Activity of CeO2–TiO2 for Chlorinated VOCs Degradation

Physical properties and photocatalytic activity of Cr-doped TiO2 nanoparticles

Visible-light Deposition of CrOx Cocatalyst on TiO2: Cr Valence Regulation for Superior Photocatalytic CO2 Reduction to CH4

Visible-light simultaneous photocatalysis of methyl orange and Cr(VI) in water by rare earth modified titanium dioxide

Strengthened Removal of Tetracycline by a Bi/Ni Co-Doped SrTiO3/TiO2 Composite under Visible Light

Defect Chemistry of Er3+-Doped TiO2 and Its Photocatalytic Activity for the Degradation of Flowing Gas-Phase VOCs

Visible-light-driven CQDs/TiO2 photocatalytic simultaneous removal of Cr(VI) and organics: Cooperative reaction, kinetics and mechanism

Visible Light-Driven Photocatalysis of Al-Doped SrTiO3: Experimental and DFT Study

Preparation of Co- and Cr-Doped Mixed Crystal Tio2 Powders and Comparison of the Photocatalytic Degradation Abilities under Sunlight Irradiation

Preparation, Characterization, and Photocatalytic Activity of Visible Light Driven Chlorine-Doped Tio2

Crystal Engineering of TiO 2 for Enhanced Catalytic Oxidation of 1,2-Dichloroethane on a Pt/TiO 2 Catalyst

Hydrothermal synthesis of Nb5+-doped SrTiO3 mesoporous nanospheres with greater photocatalytic efficiency for Cr(VI) reduction

Visible-light deposition of CrO cocatalyst on TiO2: Cr valence regulation for superior photocatalytic CO2 reduction to CH4

Efficient Visible-Light-driven Photocatalytic H2 Production over Cr/N-codoped SrTiO3

Coll 282-Photocatalytic Degradation Of Gaseous Toluene Over N-Doped Nanocrystalline Tio2 With Enhanced Activity Under Uv And Visible Light Irradiation

Photocatalytic Removal of Diclofenac by Ti Doped BiOI Microspheres under Visible Light Irradiation: Kinetics, Mechanism, and Pathways

Preparation of mesoporous strontium carbonate nanospheres with the enhanced photoactivity for TC degradation under visible light