Abstract:Ce-modified Mn-Fe mixed-oxide catalysts were prepared by a citric acid sol-gel method and characterized by X-ray diffraction, Raman, N-2 adsorption-desorption, infrared spectra, H-2 temperature-programmed reduction and thermogravimetric analyses. Their catalytic properties were investigated in ozone (O-3) decomposition reaction. Results show that the small amount of rare earth metal Ce added during Mn-Fe (FM) mixed-oxide synthesis greatly improves the catalytic performance in O-3 decomposition. Among the prepared catalysts, the C-0.04(FM)(0.96) mixed-oxide catalyst exhibits the highest catalytic activity and stability. The O-3 conversion over C-0.04(FM)(0.96 )is 98% after 24 h reaction at 25 degrees C under dry condition, and that over FM decreases to 90% after 16 h reaction. At 0 degrees C, the O-3 conversion over Ca-0.04(FM)(0.96) is 95% after 7 h reaction under dry condition, and that over FM slows down to 70%. Under humid condition (RH = 65%), the O-3 conversion over C-0.04(FM)(0.96) is 63% after 6.5 h reaction at 25 degrees C, while that over FM decreases to 55%. When Ce is doped into Mn-Fe mixed oxides, the small amount of Ce enters the crystal lattice of MnO2, and partial Fe is separated to form Fe2O3. This changes cause lattice distortion and increase defects and enable the as-synthesized Ce-Fe-Mn ternary mixed-oxide catalysts to acquire additional oxygen vacancies and increase their specific surface area, thereby increasing the number of reaction sites and enhancing the catalytic performance of the catalysts for O-3 decomposition. (C) 2020 Published by Elsevier B.V. on behalf of Chinese Society of Rare Earths.

Transition Metal Doping Effect and High Catalytic Activity of CeO2–TiO2 for Chlorinated VOCs Degradation

Insight into the Promotional Effect of CE Doped in (feconicrmn)3o4 High Entropy Oxides for Solvent-Free Aerobic Oxidation of Benzyl Alcohol

Deep Oxidation of Chlorinated VOCs over CeO2-based Transition Metal Mixed Oxide Catalysts

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Accelerating Effect of ZrO 2 Doping on Catalytic Performance and Thermal Stability of CeO 2 –cro X Mixed Oxide for 1,2-Dichloroethane Elimination

Ce–Fe–Mn Ternary Mixed-Oxide Catalysts for Catalytic Decomposition of Ozone at Ambient Temperatures

Promotional effect of doping Cu into cerium-titanium binary oxides catalyst for deep oxidation of gaseous dichloromethane

New Insight into the Structure of CeO2–TiO2 Mixed Oxides and Their Excellent Catalytic Performances for 1,2-Dichloroethane Oxidation

Promotion Effects of Ce-Doping on Catalytic Oxidation of Ethane over Pt/CexTi1−xO2

Catalytic Oxidation of Chlorinated Volatile Organic Compounds over MO_x-CeO_2/HZSM-5 Catalysts

High Activity of CeO2-TiO2 Composites for Deep Oxidation of 1,2-Dichloroethane

New Insight into the Design of Highly Dispersed Pt Supported CeO2-TiO2 Catalysts with Superior Activity for VOCs Low-Temperature Removal

Promoting Effect of Nb Doping on Catalytic Performance for Deep Oxidation of 1, 2-Dichloroethane over (ce,cr) X O 2 -Nb 2 O 5 Catalysts

Operando Investigation of Catalytic Trichloroethylene Combustion Via Metal-Doped CeO2 Nanorods

Controlled reaction depth by metal (M=Fe, Ni, Mn and Ti) doped ceria in selective oxidation of ethane with carbon dioxide

Elimination of 1,2-dichloroethane over (Ce, Cr)xO2/Nb2O5 catalysts: synergistic performance between oxidizing ability and acidity

High Catalytic Performances of CeO2–CrOx Catalysts for Chlorinated VOCs Elimination

Promoting effect of Ce doping on catalytic performance and water resistance ability for toluene catalytic combustion over the cheap and efficient Mn8Ni2CeaOx catalysts

Transition-Metal-Doped CeO2 for the Reverse Water-Gas Shift Reaction: An Experimental and Theoretical Study on CO2 Adsorption and Surface Vacancy Effects

Enhanced catalytic performance for toluene combustion via Ce-doped α-MnO2: efficient balance between toluene adsorption and activation oxidation

Elimination of 1,2-Dichloroethane over (Ce,cr)(x)o-2/Moy Catalysts (M =ti, V, Nb, Mo, W and La)