Abstract:Highly oriented titania nanotube (TN) arrays with {1 0 1} crystal face were prepared on the surface of titanium substrate by liquid chemical deposition method. The obtained titania samples were characterized by X-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), BET measurements, diffuse reflectance spectroscopy (DRS), and electron paramagnetic resonance (EPR) spin trap technique. Results indicate that the nanotubes grown in this study are well-aligned and organized into high-density uniform arrays. The typical dimensions of the hollow tube are ∼90 nm in outer diameter, ∼60 nm in inner diameter, ∼15 nm in wall thickness and ∼300 nm in height. The BET surface area of the obtained titania nanotube is 275 m2/g. The EPR signals reveal that hydroxyl radical (OH) species can be produced in the nanotube system, and no OH radical EPR signals were detected under dark and/or nanotube non-existing situations. The catalytic degradation of a textile azo dye, acid orange 7 (AO7), in aqueous solution with titania nanotube arrays electrode was carried out using photo-electrocatalytic (PEC) process, comparing with electrochemical process (EP) and photocatalytic (PC) process. A significant photo-electrochemical synergetic effect was observed, which is due to the efficient charge separation and transfer at the surface-interface of titania nanotube arrays. The kinetic constant of PEC degradation of AO7 using TN electrode was 48.7%, which is higher than that using P-25 TiO2 film and TiO2 particular film electrode. The enhanced degradation rate of AO7 using titania nanotube arrays could be attributed to their larger specific surface area and nanotubular structure with preferred reactive crystal face, which would increase their absorption capacity to the targeted substrates and the rate of surface-interface charge transfers in titania nanotube semiconductor redox systems.

Oxygen vacancy modulation of titania nanotubes by cathodic polarization and chemical reduction routes for efficient detection of volatile organic compounds

Self‐Organized TiO2 Nanotube Array Sensor for the Determination of Chemical Oxygen Demand

Amorphous Tio(2) Nanotube Arrays For Low-Temperature Oxygen Sensors

Titanium Oxide Nanotube Arrays And Their Applications

The controlled deposition of metal oxides onto carbon nanotubes by atomic layer deposition: examples and a case study on the application of V2O4 coated nanotubes in gas sensing

The Role of Lattice Defects on the Optical Properties of TiO2 Nanotube Arrays for Synergistic Water Splitting

Fabrication and Hydrogen Sensing Properties of Titania Nanotubes

Designing TiO 2 Nanotubular Arrays with Au-CoO x Core-Shell Nanoparticles for Enhanced Photoelectrochemical Methanol and Lignin Oxidation

The formation and detection techniques of oxygen vacancies in titanium oxide-based nanostructures

Fabrication and Photo-Electrocatalytic Properties of Highly Oriented Titania Nanotube Arrays with {1 0 1} Crystal Face

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Hydrogen sensing using titania nanotubes

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Surface Carbon Layer and Visible-Light Photocatalytic Activities of Carbon-Coated Tio (2) Nanotubes Synthesized in Organic Electrolytes

A Novel CO Sensor Based on the Point Contact Between Pd Decorated TiO2 Nanotubes Array

Synthesis and Study of SrTiO3/TiO2 Hybrid Perovskite Nanotubes by Electrochemical Anodization

Synthesis and characterization of TiO2 nanotubes for humidity sensing

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Boron-doped TiO2 Nanotube Array: in Situ Electrochemical Preparation and Study on Its Photocatalytic Activity

Defective TiO2 Nanotube Arrays for Efficient Photoelectrochemical Degradation of Organic Pollutants

Synthesis and Characterization of TiO2 Nanotubes for High-Performance Gas Sensor Applications