Abstract:The microstructure and mechanical properties of Fe-0.19C-1.46Mn-1.50Si, a low-carbon hot-rolling direct quenching and partitioning steel, were investigated, and particular emphasis was placed on the effects of the rolling temperature and the subsequent cooling method. Once rolling occurred above the recrystallization temperature, the grain size of prior austenite could be reduced from ∼88.2 to ∼11.8 μm. The corresponding packet and block sizes of martensite could be reduced from ∼17.6 to ∼4.3 μm and from ∼9.0 to ∼1.8 μm, respectively, after a typical two-step quenching and partitioning (Q&P) treatment following rolling immediately. Once rolling occurred below the recrystallization temperature, deformed prior austenite with a grain length and width of ∼150 and ∼60 μm, respectively, were obtained. Consequently, only the block size would be reduced to ∼1.9 μm. The volume fraction of retained austenite (RA), which was ∼11% in the specimens, was not significantly affected by the rolling temperature. Further, if the typical two-step Q&P treatment was replaced by air cooling after the rolled specimen was quenched to the martensitic start temperature, the volume fraction of RA in the specimen was reduced to ∼7.4%, and the corresponding carbon depletion degree in the martensitic matrix was decreased as well. Tension and impact tests indicated that the cooling method was more critical than the rolling temperature for determining the mechanical properties. The presence of sufficient amounts of RA and carbon depletion in the refined martensitic matrix contribute to the strong strain hardening and energy absorption capabilities of the steel together. As a result, rolling at a temperature that was slightly higher than the recrystallization temperature combined with the typical two-step Q&P treatment could be an optimized process to obtain excellent comprehensive mechanical properties. In particular, the ductile-to-brittle transition temperature (DBTT) could be reduced from −10°C to −30°C.

Effective strategies for improving quenched microstructure and mechanical properties of hot-rolled seamless steel pipes

Microstructure and mechanical properties of a low-carbon HDQ&P steel

A Study Of The Optimum Quenching Temperature Of Steels With Various Hot Rolling Microstructures After Cold Rolling, Quenching And Partitioning Treatment

Effect of carbon content and microstructural refinement on the mechanical property of quenching-partitioning - tempering-treated steels

Effect of Different Quenching Methods on the Microstructure and Mechanical Properties of 30MnB5NbTi

Effect of Partitioning Treatment on the Mechanical Property of Fe-0.19c-1.47mn-1.50si Steel with Refined Martensitic Microstructure

Enhanced mechanical properties of a Fe-Mn-Al-C austenitic low-density steel by increasing hot-rolling reduction

Effect of Cold Rolling Reduction Rate on the Microstructure and Properties of Q&P Steel with a Ferrite-Pearlite Initial Structure

Effect of quenching and tempering heat treatment process on microstructure and properties of X100 pipeline steel

Enhancement of the mechanical properties of a Nb-microalloyed advanced high-strength steel treated by quenching–partitioning–tempering process

Composition and Processing of Direct-Quench Hot Rolled Steels with Ultrahigh Strength Exceeding GPa

Effect of Nb/V/Ti Microalloy on Microstructure and Properties of 16Mn Seamless Steel Pipe

Improving the Mechanical Properties of Hot Rolled Low-Carbon Copper-Containing Steel by Adjusting Quenching Roll Speed

Application of Quenching-Partitioning-Tempering Process in Hot Rolled Plate Fabrication

Microstructure Regulation and Mechanical Properties of Low-Carbon Multiphase Steels

Achieving Fine-Grained Microstructure and Superior Mechanical Property in a Plain Low-Carbon Steel Using Heavy Cold Rolling Combined with Short-Time Heat Treatment

Improving the ultimate tensile strength without loss of plasticity of quenching-partitioning steel by introducing hot deformation

EFFECT OF ACCELERATED COOLING ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CONTROLLED ROLLED PIPE LINE STEELS

New observations of the twinning effect and austenite stability in intercritical quenched and tempered steel with high strength

Mechanical behavior and strengthening mechanism of a fine-grained medium carbon steel produced via cyclic oil quenching

Upgrade Rolling Based on Ultra Fast Cooling Technology for C-Mn Steel