Abstract:Nickel based superalloys are widely used in such applications as gas turbine blades due to their excellent mechanical properties at elevated temperatures. Oxidation is one of the life limiting factors at such temperatures since it accelerates failure mechanisms, e.g. fatigue and creep. In this project, oxidation behavior of Ni-3Al-4.8Ti-9.5Co-14Cr (wt.%) superalloy was investigated under various testing conditions. The alloy was investment-cast with preferential crystal growth direction [100]. Isothermal oxidation tests were carried out at 800°C for 150h. Cyclic oxidation tests were then conducted between 100-800°C for 150 one-hour cycles. An additional one-hour cycle was tested to replicate real-life working condition of the alloy, which consisted of heating the samples up to 800°C followed by slow cooling to 400°C. During the testing, samples were periodically taken from the furnace and weighted with an accuracy of 10 -4 g to calculate the weight gain and to analyze the microstructure of formed oxide. Scanning electron microscopy (SEM) combined with energy-dispersive spectroscopy (EDS) and X-ray diffraction were used to study the microstructure of oxidation products. The results reveal that the highest amount of weight gain is obtained in isothermal testing, while the lowest in cyclic. Diffusion of Ti and Ni to the free surface results in the early-stage formation of needle-shaped oxide phases followed by severe oxidation of Cr and Al. The layer of chromium oxide is continuous while aluminum oxide is blocky at the deepest position from the free surface. Cracks form at the interface of carbide particles and gamma phase near the free surface of cyclic oxidation samples due to concentration gradient of Ni and Al. Precipitate-free zone are observed near the free surface of all the samples at the end of the tests, but internal oxidation does not occur significantly in all the samples. It is found that temperature fluctuation increases oxide spallation, which causes crack formation. At the same time, in isothermal testing, dense, crack-free layer of oxide form on the surface of superalloy.

Delayed parabolic oxidation via transient thermal exposures on a polycrystalline nickel-based superalloy

High Temperature Oxidation Behavior of Ni-based High Entropy Superalloys

Oxidation behavior of Ni-based superalloy GH738 in static air between 800 and 1000 °C

Oxidation behavior of a nickel-based single crystal superalloy at 1100 °C under different oxygen concentration

Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980 °C in air

On the Development of a Protective Oxide System in Rare Earth Oxide Coated Nickel Superalloy under Isothermal Oxidation Conditions

Understanding the Oxidation Behaviors of a Ni-Co-based Superalloy at Elevated Temperatures Through Multiscale Characterization

ISOTHERMAL OXIDATION BEHAVIOR OF A SINGLE CRYSTAL NICKEL-BASED SUPERALLOY

Microstructural evolution during exposure in air and oxidation behavior of a nickel-based superalloy

The effect of elevated air pressure on the oxidation properties of the nickel-based superalloy, RR1000, at 650°C with different surface modifications

Oxidation of Thin Nickel-Based Superalloy Specimens: Kinetics Study and Mechanical Integrity

Isothermal short‐term oxidation behavior of MAR‐M246 nickel‐based superalloy at 800°C and 1000°C

Oxidation Kinetics of Microcrystalline Ni–11.5Cr–4.5Co–0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 900 °C

Cyclic and Isothermal Oxidation Behavior of a Directionally Solidified Ni-Al-Ti-Co-Cr Superalloy

Oxidation Behaviors of NiCrCoAl Superalloy Sheet Prepared by EB-PVD at 1000℃

A study on the multiple stages of oxidation kinetics in a single crystal nickel-based superalloy

Oxidation Kinetics of Microcrystalline Ni-11.5Cr-4.5Co-0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 800 °C

Structural Evolution of a Ni Alloy Surface During High-Temperature Oxidation

Oxidation Kinetics Of Microcrystalline Ni-11.5cr-4.5co-0.5a1 Superalloy Sheet Fabricated By Electron Beam Physical Vapor Deposition At 800 Degrees C

Oxidation Behavior of GTD111 Ni-based Superalloy at 900 °C in Air

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys