Influence of Cr content on sintering, textured structure, and properties of (Hf, Zr, Ta, Cr, Ti)B 2 high-entropy boride ceramics

Yan Zhang,Lei Shan,Yan-Fu Chai,Wei-Ming Guo,Tian-Qi Zhang,Liang Xu,Jin-Ling Cong,Hua-Tay Lin,Lian-Yun Wei,Wei-Min Ma

DOI: https://doi.org/10.1016/j.ceramint.2023.01.200

IF: 5.532

2023-04-05

Ceramics International

Abstract:In order to provide insights into the influence of Cr content on the microstructure and corresponding properties of (Hf, Zr, Ta, Cr, Ti)B 2 , the effects of 10 at.% to 30 at.% Cr contents on texture development, phase composition, microstructure, and mechanical properties of (Hf, Zr, Ta, Cr, Ti)B 2 , which were prepared via a combination of boro/carbothermal reduction and SPS, were investigated in this study. The results showed that (Hf, Zr, Ta, Cr, Ti)B 2 added with 15 at.% Cr content samples formed a textured microstructure due to the formation of CrB in the (Hf, Zr, Ta, Cr, Ti)B 2 high-entropy boride powder. With the increase of Cr content up to 30 at.%, the density, grain size, and fracture toughness of (Hf, Zr, Ta, Cr, Ti)B 2 high entropy boride ceramics increased, then for higher content, they decreased, and tended to remain constant. The hardness of (Hf, Zr, Ta, Cr, Ti)B 2 decreased with the increase of Cr content. The (Hf, Zr, Ta, Cr, Ti)B 2 with 15 at.% Cr content possessed the best comprehensive mechanical performance ( H v 0.2 : TS:26.9 ± 0.8 GPa, SS: 26.5 ± 0.6 GPa; K Ic : TS:4.21 ± 0.46 MPa·m1/2, SS: 3.16 ± 0.18 MPa·m1/2) due to a combination of high relative density and unique textured structure.

materials science, ceramics