Development of Biodegradable Polyamide 4/polyvinyl Alcohol/Poly(lactic Acid) Multilayer Films with Tunable Water Barrier Property and Superior Oxygen Barrier Property
Di Zhang,Fangke Zhan,Ziying Wang,Li Wang,Yongjun Qiu,Tao Chen,Yibing Wang,Liming Zhao
DOI: https://doi.org/10.1021/acsapm.3c00230
2023-01-01
ACS Applied Polymer Materials
Abstract:Poor mechanical and barrier properties of biopolymer-basedpackagingmaterials limit their widespread applications. The combination ofbiopolymers with different nature is considered an effective strategyto obtain complementary properties, but this method is always restrictedby the incompatibility between matrices. To combine polyamide 4 (PA4)and poly-(lactic acid) (PLA), which present excellent oxygen barrierand water barrier properties, respectively, this study puts forwardthe use of polyvinyl alcohol (PVA) as a bonding layer to connect themand form the PA4/PVA/PLA multilayer films by the layer-by-layer solutioncasting method. PA4 and PLA are successfully linked through hydrogenbonding and electrostatic interactions with PVA. The cross-sectionmorphology and peel test results proved the good interlayer adhesionbetween layers. After combination with PA4, the tensile strength,elongation at break, and oxygen barrier properties of PLA were greatlyimproved. The oxygen barrier of the PA4/PVA/PLA multilayer film wasmore than 260 times higher than that of the PLA monolayer. PA4/PVA/PLAfilms presented better thermal stability, transparency, and waterbarrier properties compared to the PA4 monolayer. Besides, PA4/PVA/PLAmultilayer films presented a one-way water barrier characteristic,which made them effective in avoiding the condensation phenomenonwhen used as fruit or vegetable packaging. The study improved thepoor interfacial compatibility between PA4 and PLA and provided asimple strategy for developing sustainable packaging with excellentperformance.