Effect of foam metal on dynamic response and fatigue damage of 5182 aluminium alloy clinched joints

Lei Lei,Ye Shi,Ming Yan,Chunyu Song,Zhiqiang Zhao

DOI: https://doi.org/10.1016/j.engfailanal.2024.108001

IF: 4

2024-02-07

Engineering Failure Analysis

Abstract:In this study, 5182 aluminium alloy clinched joints and hybrid clinched joints containing Cu foam were prepared. The effect of the copper-foam sandwich on the static strength of aluminium alloy clinched joints was analysed through a static tensile-shear test. Modal analysis was conducted using the finite element simulation software, and the variation in the inherent frequency of the two joints under fatigue service was investigated through alternating fatigue-dynamic response tests. The law of asymptotic failure under fatigue service and the effect of a copper-foam sandwich on the fatigue performance of clinched joints were explored. It was concluded from the analysis that the tensile-shear strength of the clinched joints was increased by 9.14% due to the addition of the copper-foam sandwich. With fatigue accumulation in the joints, the inherent frequency curves were observed to gradually shift to the left. The tendency of inherent frequency reduction was mitigated by the copper-foam sandwich, and the ratio of inherent frequency decline was reduced. Furthermore, micromotion wear between the upper and lower sheets was effectively isolated by the copper-foam sandwich, abrasive debris between the sheets was reduced, and the process of microcrack formation and expansion was inhibited, resulting in an improved fatigue performance of the clinched joints. The variation law of inherent frequency with fatigue accumulation, as analysed in this study, provides a valuable reference for the prediction of fatigue life.

engineering, mechanical,materials science, characterization & testing