Abstract:The influence of post-build processing on the hydrogen embrittlement behavior of additively manufactured (AM) 316L stainless steel fabricated using laser powder bed fusion was assessed at both room temperature and -50$^\circ$ C via uniaxial tensile experiments. In the absence of hydrogen at ambient temperature, all four evaluated AM conditions (as-built (AB), annealed (ANN), hot isostatic pressed (HIP), and HIP plus cold worked (CW) to 30\%) exhibit notably reduced ductility relative to conventionally manufactured (CM) 316L stainless steel. The AM material exhibits sensitivity to the build direction, both in the presence and absence of hydrogen, with a notable increase in yield strength in the X direction and enhanced ductility in the Z direction. Conversely, testing of non-charged specimens at -50$^\circ$ C revealed similar ductility between the CM, AB, ANN, and HIP conditions. Upon hydrogen charging, the ductility of all four AM conditions was found to be similar to that of CM 316L at ambient temperature, with the HIP condition actually exceeding the CM material. Critically, testing of hydrogen-charged samples at -50$^\circ$ C revealed that the ductility of the HIP AM 316L condition was nearly double that observed in the CM 316L. This improved performance persisted even after cold working, as the CW AM 316L exhibited comparable ductility to CM 316L at -50 C after hydrogen charging, despite having a 2-fold higher yield strength. Feritscope measurements suggest this increased performance is related to the reduced propensity for AM 316L to form strain-induced martensite during deformation, even after significant post-processing treatments. These results demonstrate that AM 316L can be post-processed using typical procedures to exhibit similar to or even improved resistance to hydrogen embrittlement relative to CM 316L.

Hydrogen Interaction with 316L Steel Obtained by Selective Laser Melting

Significance of Melt Pool Structure on the Hydrogen Embrittlement Behavior of a Selective Laser-Melted 316L Austenitic Stainless Steel

Hydrogen embrittlement susceptibility of additively manufactured 316L stainless steel: influence of post-processing, printing direction, temperature and pre-straining

The dependence of hydrogen embrittlement on hydrogen transport in selective laser melted 304L stainless steel

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Structural and micromechanical properties of 316L stainless steel produced by selective laser melting

The difference in fatigue crack growth induced by internal and external hydrogen in selective laser melted 304L stainless steel

The high strength and hydrogen embrittlement resistance of selective laser melted 304 austenitic stainless steel

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Microstructure and Mechanical Properties of Selective Laser Melting of Hydrogen Embrittlement Resistance Stainless Steel HR-2

Mechanical properties of 316L stainless steel samples fabricated by selective laser melting and comparison with other manufacturing methods

Investigation on the Attainment of High-Density 316L Stainless Steel with Selective Laser Sintering

Effect of additive manufacturing and subsequent heat and/or surface treatment on the hydrogen embrittlement sensitivity of 316L austenitic stainless steel

Study on performance optimization of 316L stainless steel parts by High-Efficiency Selective Laser Melting

Comparative study of hydrogen embrittlement resistance between additively and conventionally manufactured austenitic stainless steels

On The Corrosion and Metastable Pitting Characteristics of 316L Stainless Steel Produced by Selective Laser Melting

Hydrogen permeation behavior and hydrogen-induced defects in 316L stainless steels manufactured by additive manufacturing

Analysis of Fatigue Properties of Selective Laser Melting 316L Stainless Workpiece After Post-heat Treatment

Anisotropy in mechanical property and hydrogen embrittlement resistance of selective laser melted 304 austenitic stainless steel

Strain-induced twins and martensite: Effects on hydrogen embrittlement of selective laser melted (SLM) 316 L stainless steel

Selective Laser Melting of Duplex Stainless Steel 2205: Effect of Post-Processing Heat Treatment on Microstructure, Mechanical Properties, and Corrosion Resistance