Belite-ye'elimite-ferrite cements produced from London Clay

Marcus Yio,Yi Ng,Pengkun Hou,Tsz Chun Chan,Hong Wong

DOI: https://doi.org/10.1680/jadcr.23.00239

IF: 2.2061

2024-09-26

Advances in Cement Research

Abstract:London Clay (LC) is generated in significant quantities from major infrastructure development projects within and around London. Excavated LC spoils are typically landfilled or used for landscaping purposes with minimal value. This study investigates the feasibility of producing belite-ye'elimite-ferrite (BYF) cements using London Clay (LC) in combination with kaolin or low-grade bauxite. Six cement clinkers with varying compositions were synthesised at 1300°C. The phase composition of the synthesised clinkers was quantified using XRD coupled with Rietveld refinement. The hydration behaviour, phase assemblage evolution, and mechanical performance of the cements were examined using isothermal calorimetry, XRD, TGA, and compressive strength testing respectively, up to 90 days of curing. It is demonstrated that LC can be used either on its own or with kaolin or low-grade bauxite to produce BYF cements with a wide range of composition: 31 to 64 wt.% belite, 9.3 to 27 wt.% ye'elimite and 2.1 to 31% ferrite. The use of LC as the sole alumina source resulted in low compressive strength at early stages. Nevertheless, the strength developed over time, reaching 27.8 MPa at 90 d (0.5 w/b). Possible approaches to develop LC further for producing viable BYF cements are discussed.

construction & building technology,materials science, multidisciplinary