Abstract:Activated carbon (AC) fiber is a carbonaceous material with a porous structure that has a tremendous scope of application in different fields. Conventionally, AC is derived from fossil fuel-based raw materials like polyacrylonitrile (PAN) and pitch. In this work, AC was synthesized from eco-friendly, renewable, and ubiquitous jute fiber. Systematically, the jute fiber was washed and pretreated with NaOH. Raw jute and NaOH-treated jute were carbonized/pyrolyzed at 500 °C for 1 h in presence of N2 gas. The carbonized carbon was activated with H3PO4 and KOH and again pyrolyzed at 650 °C for 1.5 h maintaining the inert condition. The different features of activated carbons were characterized with field emission-scanning electron microscope, energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray diffraction (XRD), and thermogravimetric analysis. The average yield of carbonized and activated carbons was recorded at 19 and 13.8%, respectively. The scanning electron microscopic images confirmed a honeycomb-like porous structure. It was observed that KOH-activated carbon exhibited a more porous structure than the H3PO4-activated carbons. The average pore diameter of activated carbons was noted to be 1.3 μm. The pore density was higher in case of KOH-activated carbons accounting for 2.15 pore/μm. The EDX analysis showed that H3PO4-activated carbons had more than 90% carbon atoms indicating a significant carbon content. The TEM images revealed that AC particles were in the nanoscale range. The average particle sizes of H3PO4-activated carbon and KOH-activated carbon were 36.38 and 32.8 nm, respectively. The XRD study demonstrated the highly disordered and low level of crystallinity of AC. It was detected that the AC showed much higher thermal resistance than the jute fiber. The H3PO4-activated carbon obtained from NaOH-treated jute remained at 84% even after 500 °C. A higher thermal resistance was achieved with H3PO4-activated carbon since it contains 0.56% phosphorus, which was confirmed by EDX investigation. It was found that a higher carbon yield was obtained from NaOH-treated jute. The porous structure of the material showed that it could be used as an adsorbent. Due to its high thermal stability, it is recommended for flame retardants and heat insulation applications as well.

The environmental impacts via life cycle assessment of activated carbon produced by Fiddlewood and Jacaranda biomass

Comparative life cycle assessment of activated carbon production from various raw materials

Effect of different activation agents for activated carbon preparation through characterization and life cycle assessment

Life cycle assessment as a comparison tool for activated carbon preparations and biomethane storage for vehicular applications

Comparative environmental impact assessment of activated carbon electrodes for supercapacitors

Sustainable production of porous carbon from biomass: Influence of pre-carbonization on pore evolution and environment impact

Recent trends in activated carbon fibers production from various precursors and applications—A comparative review

Reliable Method and Multistage Process Involved in the Production of Activated Carbon Based on Raw Material-A Systematic Review

Single-step preparation of activated carbons from pine wood, olive stones and nutshells by KOH and microwaves: Influence of ultra-microporous for high CO 2 capture

Preparation of activated carbon from biomass and its’ applications in water and gas purification, a review

Synthesis and characterizations of conocarpus- and azadirachta-derived activated carbons as wastewater recycling material

Activation of mixed sawdust and spirulina with or without a pre‐carbonization step: Probing roles of volatile-char interaction on evolution of pyrolytic products

The chemical process of producing activated carbon using walnut shells and plastic wastes

Synthesis, Activation, and Characterization of Carbon Fiber Precursor Derived from Jute Fiber

Sustainable Activated Carbon Production via Microwave for Wastewater Treatment: A Comparative Review

One-step microwave pyrolysis-H 3 PO 4 activation of woody biomass: Insight into the product characteristics and life cycle assessment

A review on utilization of wood biomass as a sustainable precursor for activated carbon production and application

Prospective Life Cycle Assessment Prospective (LCA) of Activated Carbon Production, Derived from Banana Peel Waste for Methylene Blue Removal

Real-time monitoring the carbonization and activation process of activated carbon prepared from Chinese parasol via zinc chloride activation

Life Cycle Assessment of Biomass Pyrolysis

Systematic study of dynamic CO2 adsorption on activated carbons derived from different biomass