Abstract:Soot combustion experiments with 5%O2/He were conducted using model soot, and four distinct compositions of CexPr1-xO2-δ oxides of varying nominal cerium compositions (x = 0, 0.2, 0.3, and 1) were prepared. The catalyst samples were comprehensively characterized using techniques such as XRD, Raman spectroscopy, HR-TEM, N2 adsorption at −196 °C, XPS, O2-TPD, H2-TPR, and work function measurements. The Pr-rich compositions, ranging from Ce0.3Pr0.7O2-δ to PrO2-δ, resulted in a significant increase in the total evolved O2 amounts and enhanced catalyst reducibility. However, a decrease in the textural properties of the catalysts was noted, which was particularly important for the pure praseodymia under the synthesis route conducted. The catalytic activity was investigated under the two following contact modes of mixing between soot and catalyst: loose and tight. The results revealed that the catalytic performance is associated with the surface contact in tight contact mode and with the combination of surface/subsurface/bulk oxygen mobility and the BET surface area in loose contact mode. Notably, the temperatures estimated at 10% and 50% of the conversion (T10 and T50) parameters were achieved at much lower temperatures than the uncatalyzed soot combustion, even under loose contact conditions. Specifically, the 50% conversion was achieved at 511 °C and 538 °C for Ce0.3Pr0.7O2 and Ce0.2Pr0.8O2, respectively. While no direct correlation between catalytic activity and work function was observed, a significant relationship emerges between work function values and the formation of oxygen vacancies, whatever the conditions used for these measurements. On the other hand, the ability to generate a high population of oxygen vacancies at low temperatures, rather than the direct activation of gas-phase O2, influences the catalytic performance of Pr-doped ceria catalysts, highlighting the importance of surface/subsurface oxygen vacancy generation, which was the parameter that showed a better correlation with the catalytic activity, whatever the soot conversion value or the mode of contact considered.

Study on the purification performance of modified La–Ni based perovskite catalysts co-doped with metal K and Pr for simultaneous removing soot particles and NOx of diesel engine exhaust

Preparation, Structure and Soot Oxidation Performance of Nano-scaled Perovskite-type La1-xKxCoO3 Catalyst

Efficient Catalysts of K and Ce Co-Doped LaMnO 3 for NO x –Soot Simultaneous Removal and Reaction Kinetics

Efficient Catalysts of K and Ce Co-Doped LaMnO3 for NOx–Soot Simultaneous Removal and Reaction Kinetics

NO2-aided Soot Oxidation on LaMn0.7Ni0.3O3 Perovkite-type Catalyst

Preparation, Characterization, Catalytic Activity and CO2 Absorption/desorption Studies of Ln/K (ln=la, Sm, Y) Catalysts for Diesel Soot Elimination

Study of Ce, Ca, Fe, and Mn-Doped LaCoO3 Perovskite Oxide for the Four-Way Purification of PM, NOx, CO, and HC from Diesel Engine Exhaust

Mechanism of Pd and K co-doping to enhance the simultaneous removal of NO<sub>x</sub> and soot over LaMnO<sub>3</sub>

Facile preparation of Fe-Beta zeolite supported transition metal oxide catalysts and their catalytic performance for the simultaneous removal of NO x and soot

Dispersed Pr on Nickel Oxide for Efficient Nitrous Oxide Direct Decomposition in Simulated Nitric Acid Exhaust

Preparation, Characterization and Catalytic Activity Studies of CeO2–K Diesel Soot Oxidation Catalysts Loaded on Porous Al2O3 Substrate Using Water-Immiscible Solvent

Ni-BaMnO3 Perovskite Catalysts for NOx-Assisted Soot Oxidation: Analyzing the Effect of the Nickel Addition Method

Preparation of Cordierite Monolith Catalysts with the Coating of K-Modified Spinel MnCo2O4 Oxide and Their Catalytic Performances for Soot Combustion

Mechanism of Pd and K Co-Doping to Enhance the Simultaneous Removal of NOxand Soot over LaMnO3

Promoting Soot Combustion Efficiency by Strengthening the Adsorption of NOx on the 3DOM Mullite Catalyst

Diesel soot oxidation over potassium-promoted urchin-structured NiO-NiCo2O4 catalyst

Nanostructured Pr-Rich CexPr1-xO2-δ Mixed Oxides for Diesel Soot Combustion: Importance of Oxygen Lability

Reaction pathway of nitric oxide oxidation on nano-sized Pt/SiO2 catalysts for diesel exhaust purification

Performance of soot oxidation by O 2 /NO/N 2 atmosphere in various catalyst species

Cerium Doping Effect in 3DOM Perovskite-Type La2−xCexCoNiO6 Catalysts for Boosting Soot Oxidation

Research progress on the preparation of alkali/alkaline earth metal-modified metal oxide catalysts and their application to diesel engine exhaust soot particle catalytic purification