Sol-gel synthesis and photocatalytic activity of In0.05TiO2(x)/HGB composite suspended in azophloxine solution

Meihua Lian,Wenjie Zhang,Ming Han

DOI: https://doi.org/10.1007/s10971-023-06304-6

2024-01-11

Journal of Sol-Gel Science and Technology

Abstract:Low-density In 0.05 TiO 2 ( x )/HGB composite was synthesized by loading indium doped titanium dioxide onto hollow glass bubbles (HGB) via a sol-gel route ( x is the weight content of In 0.05 TiO 2 in the composite, and n (In): n (Ti) is 0.05:1.). The dispersion of In 0.05 TiO 2 onto the surface of HGB slightly reduced the crystallite size of anatase TiO 2 . The bandgap energies of In 0.05 TiO 2 ( 20 )/HGB, In 0.05 TiO 2 ( 30 )/HGB, In 0.05 TiO 2 ( 60 )/HGB and In 0.05 TiO 2 were calculated to be 3.28, 3.21, 3.15 and 3.10 eV, respectively. The BET surface area of the pure In 0.05 TiO 2 is 36.4 m 2 /g, and the pore volume is 0.0575 cm 3 /g. Both the BET surface area and pore volume of the In 0.05 TiO 2 ( x )/HGB composites are reduced with a decreasing In 0.05 TiO 2 content. If In 0.05 TiO 2 content is more than 40%, the photocatalytic activities of the composites are almost as strong as that of the pure In 0.05 TiO 2 . The azophloxine solution was completely decolorized after 90 min in the presence of In 0.05 TiO 2 ( 60 )/HGB or pure In 0.05 TiO 2 . The activity of the composites has a close correlation with the produced hydroxyl radicals. The In 0.05 TiO 2 ( x )/HGB composites can float on the surface of the azophloxine solution after the photocatalytic reaction, so the material can be easily collected for the next treatment cycle.

materials science, ceramics