Abstract:In the presented work, the mechanism of evolution of defects in the crystalline structure after irradiation with 1500 kGy and 3000 kGy absorption dose at room temperature in a 60 Co gamma source was studied, using 43 nm sized ZrB 2 crystals. The crystals were characterized by a purity of 99.9%, a powder density of 0.23 g/cm 3 , a specific surface area of 80 to 120 m 2 /g, and a hexagonal P6/m mm spatial structure. The dose rate applied was 6.05 Gy/s, with 1.17 and 1.37 MeV energy lines. The effect of particles resulting from the decay of Na 22 radioactive isotope β + with an activity of 10.5 μCi, as well as gamma quanta with an energy of 1.27 MeV, on the core and valence electrons and vacancies in the crystal structure was studied using Positron Annihilation Lifetime Spectroscopy (PALS) and Doppler broadening analysis methods. Additionally, the changes in the S and W parameters, which characterize the distribution of defects within the volume of the ZrB 2 crystal, were studied using the Doppler broadening method. For unannealed material, the positron lifetime τ 1 component varied between 174±2 ps and 181±1 ps. After annealing, the positron lifetime component τ 2 was decreased from 290±3 ps to 226±3 ps, and the intensity component I 2 increased from 17.49% to 40 % depending on the radiation dose. The calculated values of the positron lifetime τ for one boron vacancy from ABINIT and MIKA packages were found to be 172 ps and 145 ps, respectively. The material was observed to satisfy the necessary functional conditions at gamma doses not exceeding 3000 kGy.

Exploring nanovoids in spinel ceramics using positron–positronium trapping model

Positron Annihilation Lifetime Spectroscopy Insight on Free Volume Conversion of Nanostructured MgAl2O4 Ceramics

Hydroxyl Defects and Oxide Vacancies Within Ringwoodite—toward Understanding the Defect Chemistry of Spinel-Type Oxides

Direct Control of Defects on Positron Lifetimes and Dielectric Constant of Microwave Ceramics

Nanocrystalline Si Studied by Beam-Based Positron Annihilation Spectroscopy

Co-catalysed VLS Growth of Novel Ceramic Nanostructureselectronic Supplementary Information (ESI) Available: TEM, SEM and HRTEM Images for MgO, SiOx and AlOx Ceramic Nanomaterials. See Http://Www.rsc.org/suppdata/jm/b3/b312498n/

Enhanced nucleation of Ag nanoparticles by vacancy-type defects in Ar-ions implanted spinel

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

Positron annihilation spectroscopy of the interface between nanocrystalline Si and SiO2

First-principles calculations for intrinsic defects in MgO: Positron lifetime and momentum distribution of electron-positron pairs

Probing defects in chemically synthesized ZnO nanostrucures by Positron Annihilation and Photoluminescence Spectroscopy

Probing Spin Waves in Co3O4 Nanoparticles for Magnonics Applications.

Distinctive features of diffusion-controlled radiation defect recombination in stoichiometric magnesium aluminate spinel single crystals and transparent polycrystalline ceramics

Evolution of Native Point Defects in ZnO Bulk Probed by Positron Annihilation Spectroscopy

Parallel pumping of magnons in inhomogeneous spin textures probed through NV spin relaxometry

Investigating the impact of gamma irradiation and temperature on vacancy formation and recombination in ZrB 2 ceramics using positron annihilation spectroscopy

Engineering spin defects in hexagonal boron nitride

An NV- center in magnesium oxide as a spin qubit for hybrid quantum technologies

Spin Model of O2-based Magnet in a Nanoporous Metal Complex

Nuclear Magnetic Resonance Spectroscopy for In Situ Monitoring of Porous Materials Formation under Hydrothermal Conditions

17O Solid-State NMR Studies of ZrO2 Nanoparticles