Abstract:316 stainless steel (SS) was coated with CoCrFeNiNbx (x: atomic ratio, x = 0, 0.1, 0.2, and 0.3) high entropy alloy coatings (HEACs) by laser cladding (LC). The impacts of Nb content on the phase composition, microstructure, microhardness, wear resistance and corrosion properties of CoCrFeNi based HEACs were examined. Different from the canonical dendritic (DR) - interdendritic (ID) microstructure presented by the other three HEACs, the ID of Nb0.3 HEACs also existed nanoscale Nb-rich Laves phase composed of Nb-Ni and Nb-Co. The inclusion of Nb significantly reduced the average grain size of CoCrFeNi based HEACs from 59.43 mu m to 11.38 mu m. It also greatly diminished the formation of high angle grain boundaries (HAGBs), increasing the percentage of low angle grain boundaries (LAGBs) from 31 % to 61 %. The microhardness of Nb-containing HEACs was significantly promoted due to the solid solution strengthening and fine grain strengthening caused by large size Nb atoms. Affected by Laves phase with high coordination number and space filling ratio and higher proportion of LAGBs, the microhardness of Nb0.3 HEAC was even as high as 530 HV. The increase in Nb concentration also strengthened the HEACs' resistance to wear. Nb0, Nb0.1, Nb0.2, and Nb0.3 HEACs had corresponding specific wear rates of 0.36, 0.32, 0.23, and 0.20 mm3/Nm. Unlike 316 SS, Nb0 and Nb0.1 HEACs, which had both adhesive wear and abrasive wear, Nb0.2 and Nb0.3 HEACs were mainly wear by abrasive wear. The corrosion behavior of CoCrFeNiNbx HEACs in 0.5 M H2SO4 solution was similar to 316 SS, but the corrosion resistance was stronger than 316 SS. Nb0.3 HEAC with the Ecorr of -164 mV and Icorr of 6.40 x 10-7 A/cm2 showed the best acid corrosion resistance, which could be attributed to the stable and dense passivation film on its surface. Distinct from the intergranular corrosion of other coatings, the corrosion of Nb0.3 HEAC mainly occurred in DR, because the FCC phase acted as the anode site in it when FCC and Laves phase co-existed.

Comparing the Corrosion Behavior of CoCrNi Medium-Entropy Alloy and Duplex Stainless Steel in Ammonium Chloride Solution

A comparative study on the corrosion behavior of CoCrNi medium-entropy alloy and 316L stainless steel in simulated marine environment

Corrosion Behavior of CoCrNi Medium-Entropy Alloy in NH4Cl Solution with Different pH

Corrosion Resistance of CoCrFeMnNi High Entropy Alloy Compared with 2205 Duplex Stainless Steel in a Simulated Concrete Pore Solution

Electrochemical Corrosion Behavior in Sulfuric Acid Solution and Dry Sliding Friction and Wear Properties of Laser-Cladded CoCrFeNiNb High Entropy Alloy Coatings

A comparison of the mechanical and corrosion behavior of Fe49.5Mn25Cr15Ni10C0.5 medium-entropy alloy with its subsystems steels

Corrosion behavior and mechanism of FeCrNi medium entropy alloy prepared by powder metallurgy

Interstitial nitrogen enhances corrosion resistance of an equiatomic CoCrNi medium-entropy alloy in sulfuric acid solution

Comparative corrosion behavior of Fe50Mn30Co10Cr10 dual-phase high-entropy alloy and CoCrFeMnNi high-entropy alloy in 3.5 wt% NaCl solution

Susceptibility of chloride ion concentration, temperature, and surface roughness on pitting corrosion of CoCrFeNi medium‐entropy alloy

Mechanical Property Comparisons Between CrCoNi Medium-Entropy Alloy and 316 Stainless Steels

Corrosion performance of selective laser-melted equimolar CrCoNi medium-entropy alloy vs its cast counterpart in 3.5 wt% NaCl

Microstructure, Mechanical and Corrosion Properties of Al–Co–Cr–Ni Near-Eutectic Medium Entropy Alloys

Comparative Study of Mechanical and Corrosion Behaviors of Cost-Effective AlCrFeNi High Entropy Alloys

The Comparative Investigation of Corrosion Behavior of a Cast Lean Duplex and Austenitic Stainless Steels in Chloride Environment

Corrosion behavior of AlCoCrFeNi2.1 eutectic high-entropy alloy in Cl--containing solution

Microstructure and Corrosion Properties of Crmnfeconi High Entropy Alloy Coating

The effect of Co substitutions for Ni on microstructure, mechanical properties and corrosion resistance of Fe50Mn25Cr15Ni10 medium-entropy alloy

A Comparative Study on Corrosion Behaviors of Fe35Mn10Cr20Ni35 High‐Entropy Alloy and 304 Stainless Steel in Sulfuric Acid Aqueous Solution

The effect of Mn addition on corrosion behaviour of equiatomic CoCrFeNi high entropy alloys in NaCl solution

Microstructure and corrosion behavior of Co-free FeCrNiSi0.4 medium entropy alloy coating fabricated by laser cladding