Abstract:Homogenously doped and mixed yttria stabilized zirconia, YSZ (with 3 and 10mol% Y2O3 known as 3YSZ and 10YSZ) and NiO/10YSZ co-precipitates (nominally corresponding to 7, 12, 24, 30, 35 and 45vol.% Ni metal), were synthesized using a continuous hydrothermal flow synthesis (CHFS) system which uses a stream of superheated water at 450°C and 24.1MPa as a reaction medium to cause rapid precipitation of metal oxide nanoparticle co-precipitates from a mixed metal salt solution. All products were obtained directly from the outlet of the CHFS reactor as a slurry, which was then cleaned and freeze-dried prior to further processing. The highly crystalline nano-powdered products were characterized using a range of analytical methods, including: powder X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), Raman spectroscopy and BET surface area measurements. Spherical primary particles of 10YSZ and 3YSZ were observed under the TEM and found to be 5.0±0.8nm (range 3.2–6.3nm) and 6.2±1.4nm (range 3.3–8.4nm) in size, with measured BET surface areas of 160.6 and 241.7m2g−1, respectively. Sintering of the nano-powder co-precipitates was performed via spark plasma sintering (SPS) at 1100°C for 1min, leading to densities of ca. 98% for 10YSZ and ca. 96% for Ni/10YSZ cermets (all NiO was converted into Ni due to the reducing atmosphere of the SPS). The 24% Ni/10YSZ cermet was subjected to focused ion beam tomography, which allowed the 3D arrangement of the conducting Ni metallic network of the dense cermet to be elucidated, and showed that a complete 3D network of Ni existed throughout the dense cermet disk. Electrical conductivity tests showed that the samples exhibited higher than expected electrical conductivity (for such low metal content), e.g., the 24vol.% Ni-containing sample achieved an electrical conductivity of ∼200Scm−1 at the fuel cell operating temperature, which corresponds to an effective conductivity of ∼117Scm−1 if a porosity of 30% were to be introduced.

Design of core-shell structured YSZ@Cu cermet powders with thermal conductivity anisotropy by electroless deposition

Effect of the core-shell structure powders on the microstructure and thermal conduction property of YSZ/Cu composite coatings

Core-shell Structured YSZ/CeO 2 Composite Thermal Barrier Coating Fabrication and Properties

Highly conductive low nickel content nano-composite dense cermets from nano-powders made via a continuous hydrothermal synthesis route

Influence of Microstructure on Thermal Conductivity of Plasma-Sprayed YSZ Coating

Structural Optimization for the Thermal Conductivity and Thermal Cycling Behavior in Thermal Barrier Coatings and Analysis of Thermomechanical Properties by Computational Investigation

The Effect of Two Raw YSZ Materials with Different Morphology on TBCs Via Atmospheric Plasma Spraying: Microstructures and High-Temperature Performance

Study of microstructure, electronic structure and thermal properties of Al2O3-doped tetragonal YSZ coatings

Assessment of the Performance of Y2SiO5-YSZ/YSZ Double-Layered Thermal Barrier Coatings

Sintering Behavior of a Nanostructured Thermal Barrier Coating Deposited Using Electro‐sprayed Particles

Effect of doping CeO2 and Sc2O3 on structure, thermal properties and sintering resistance of YSZ

Thermal Cycling Performance of La2Ce2O7/50 Vol.% YSZ Composite Thermal Barrier Coating with CMAS Corrosion

Fabrication and Characterization of CeO2-Doped Yttria-Stabilized ZrO2 Composite Particles

RELATION BETWEEN MICROSTRUCTURE AND THERMAL CONDUCTIVITY OF PLASMA-SPRAYED 8YSZ COATING

A novel structure design towards extremely low thermal conductivity for thermal barrier coatings - Experimental and mathematical study

Improved Properties of Scandia and Yttria Co-Doped Zirconia As a Potential Thermal Barrier Material for High Temperature Applications

Preparation and High-Temperature Performance of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coatings

Preparation and Thermal Cycling Performance of Ce-doped YSZ Thermal Barrier Coatings by a Novel Cathode Plasma Electrolytic Deposition

A novel strategy to control the microstructure of plasma-sprayed YSZ thermal barrier coatings

Wide-velocity Range High-Energy Plasma Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coating — Part II: Structural Defects and Thermal-Bonding Properties

Phase Composition and Stability, Sintering and Thermal Conductivity of Gd2O3 and Yb2O3 Co-Doped YSZ