Electrochemical properties of La1.5Pr0.5Ni0.95−Cu Al0.05O4+ Ruddlesden-Popper phase as cathodes for intermediate-temperature solid oxide fuel cells

Qingjun Zhou,Ting Zhang,Chen Zhao,Liangwu Qu,Yong He,Tong Wei,Xiaoqiang Tong

DOI: https://doi.org/10.1016/j.materresbull.2020.110986

IF: 5.6

2020-11-01

Materials Research Bulletin

Abstract:The Ruddlesden-Popper materials La1.5Pr0.5Ni0.95− x Cu x Al0.05O4+ δ (x = 0, 0.1, 0.25, 0.5, 0.75, 0.95), La1.5Pr0.5NiO4+ δ , and La1.5Pr0.5CuO4+ δ have been synthesized by the sol-gel method as cathode materials on the SDC (Sm0.2Ce0.8O1.9) electrolyte for intermediate-temperature solid oxide fuel cells (IT-SOFCs). The cathode materials sintered at 700 and 800 °C for 72 h, also showing good phase stability. The maximum conductivity of this series reached approximately 50 S cm−1 at 350 °C with x = 0.25. The lowest area-specific resistance (ASR) of the cathode measured on the SDC was 0.04 Ω cm2 at 800 °C with x = 0.1. The maximum power density of the SDC-supported single-cell reached 530 mW cm−2 at 800 °C with x = 0.1. Among all of the samples, La1.5Pr0.5Ni0.85Cu0.1Al0.05O4+ δ exhibited excellent electrochemical performance, making it a promising candidate cathode material for IT-SOFCs.

materials science, multidisciplinary