Abstract:When the nanoscale zero valent iron (nZVI) is used for the reduction of hexavalent chromium (Cr6+) to trivalent chromium (Cr3+) in groundwater, the reduction efficiency is decreased due to the passivation of reactive sites by precipitation. The bimetallic nanoparticle (BNP) can be created with the addition of the second metal to achieve a higher activity and reduce the occurrence of the ferrous/ferric hydroxide precipitation. In this study, the iron-coated aluminum (Fe/Al) BNP and aluminum-coated iron (Al/Fe) BNP systems were designed for remediating Cr6+-contaminated groundwater. The chemical liquid-phase deposition and co-reduction method was applied to produce BNPs. Cr6+ removal rate by Fe/Al BNPs was directly proportional to the saturation concentration and reactive sites, which caused a higher Cr6+ removal rate. The pseudo-first-order kinetic model could be used to describe the Cr6+ adsorption mechanism by Fe/Al BNPs. Results show that Fe/Al BNPs and Al/Fe BNPs could reduce Cr6+ to Cr3+, and the removal efficiencies for Cr6+ were 1.47 g/g BNP and 0.07 g/g BNP, respectively. Detection of Cr3+ in the aqueous phase was observed during the Cr6+ removal process. Results from X-ray diffraction (XRD) analysis confirmed that Cr(OH)3 was present on the surface of BNPs. Main mechanisms caused Cr6+ removal included reduction, precipitation, and adsorption. The reduction of Cr6+ produced OH−, which created alkaline environment and facilitated the formation of chromium hydroxide precipitates [Cr(OH)3]. Thus, the migration of Cr3+ was prevented and the environmental risk was reduced. BNP had a higher activity and stability, and it was applicable for Cr6+-contaminated site remediation.

Reduction of hexavalent chromium mediated by micro- and nano-sized mixed metallic particles

[Simultaneous Remediation of Cr (VI) and P-Ncb by Nanosacle Iron].

Removal of Hexavalent Chromium from Wastewater by Cu/Fe Bimetallic Nanoparticles

Facile Improvement of Nanoscale Zero-Valent Iron Activity with Exceptional Stability for Reduction of Cr(VI)

Fe–Ni/MWCNTs Nano-Composites for Hexavalent Chromium Reduction in Aqueous Environment

Chromium (VI) Reduction in Aqueous Solutions by Fe3O4-stabilized Fe0 Nanoparticles

Reduction of Hexavalent Chromium by Carboxymethyl Cellulose-Stabilized Zero-Valent Iron Nanoparticles

Rapid and efficient reduction of chromate by novel Pd/Fe@biomass derived from Enterococcus faecalis

“In-situ synthesized” iron-based bimetal promotes efficient removal of Cr(VI) in by zero-valent iron-loaded hydroxyapatite

Ni–Fe/Reduced Graphene Oxide Nanocomposites for Hexavalent Chromium Reduction in an Aqueous Environment

Reclamation of hexavalent chromium using catalytic activity of highly recyclable biogenic Pd(0) nanoparticles

Kinetics of Hexavalent Chromium Reduction by Iron Metal

Palladium nanoparticles supported on aluminum oxide (Al2O3) for the catalytic hexavalent chromium reduction

Preparation of highly dispersive and antioxidative nano zero-valent iron for the removal of hexavalent chromium

Removal of hexavalent chromium from aqueous solution by fabricating novel heteroaggregates of montmorillonite microparticles with nanoscale zero-valent iron

Microwave-assisted synthesis of Pd-Ru-Re/f-MWCNTs nanocatalyst for efficient catalytic reduction of chromium and pesticide

Reduction and removal of Cr(VI) in water using biosynthesized palladium nanoparticles loaded Shewanella oneidensis MR-1

Application of iron/aluminum bimetallic nanoparticle system for chromium-contaminated groundwater remediation

Granulation for extended-release of nanoscale zero-valent iron exemplified by hexavalent chromium reduction in aqueous solution

Polyacrylate stabilized ZVI/Cu bimetallic nanoparticles for removal of hexavalent chromium from wastewater