Granulation for extended-release of nanoscale zero-valent iron exemplified by hexavalent chromium reduction in aqueous solution

Yu-Jen Shih,Chiu-Wen Chen,Kuo-Feng Hsia,Cheng-Di Dong

DOI: https://doi.org/10.1016/j.seppur.2015.10.043

IF: 8.6

2015-12-01

Separation and Purification Technology

Abstract:Granulated nanoparticles of zero-valent iron (GnZVI) was prepared for enhancing the efficacy of Fe0 on remediation of Cr(VI)-containing wastewater under various experimental conditions (iron dose, initial Cr(VI) level and pH). A borohydride reduced iron substrate stabilized with polymeric surfactant (PV3A) constituted the GnZVI, whose primary grain size was averagely below 10nm by XRD analysis and the granulated pellet grown up to around five micrometers in diameter under SEM observation. Granulation was found to exert an obvious retarding effect on Cr(VI) removal by Fe0 nanoparticles based on results of kinetics using pseudo-first order rate model; at optimum conditions (initial Cr(VI)=20ppm, pH 2, iron=0.05gL−1) nZVI and GnZVI removed above 95% of Cr(VI) in 5 and 30min, respectively, whereas the highly reactive nature of nZVI that led to passivation soon after exposure to the medium could be modified by the granulated configuration. Effectiveness of GnZVI was still moderate as elevating Cr(VI) to 60ppm and pH above 4. Further, magnetite was the only oxide phase found in crystalline nZVI structure after a contact with Cr(VI)/H2O. The monitoring oxidation/reduction potential (ORP) revealed that GnZVI maintained reaction system at more reductive state than did nZVI, suggesting its relatively mild reactivity with target pollutants.

engineering, chemical