Synthesis of La0.5Ca0.5-x xMnO3 nanocrystalline manganites by sucrose assisted auto combustion route and study of their structural, magnetic and magnetocaloric properties

S. Ben Moumen,Y. Gagou,M. Chettab,D. Mezzane,M. Amjoud,S. Fourcade,L. Hajji,Z. Kutnjak,M. El Marssi,Y. El Amraoui,Y. Kopelevich,Igor A. Lukyanchuk
DOI: https://doi.org/10.1007/s10854-019-02392-9
2019-10-27
Abstract:Perovskite manganite La0.5Ca0.5-x xMnO3 (LCMO) nanomaterials were elaborated using the sucrose modified auto combustion method. Rietveld refinements of the X-ray diffraction patterns of the crystalline structure confirm a single-phase orthorhombic state with Pbnm space group (No. 62). The Ca-vacancies were voluntarily created in the LCMO structure in order to study their influence on the magnetic behaviour in the system. The magnetic susceptibility was found to be highly enhanced in the sample with Ca-vacancies. Paramagnetic-to-ferromagnetic phase transition was evidenced in both samples around 254 K. This transition is, characterized by a drastic jump of the susceptibility in the sample with Ca-vacancies. The maximum of entropy change, observed for both compounds at magnetic field of 6T was 2.30 J kg-1K-1 and 2.70 J kg-1K-1 for the parent compound and the lacunar one respectively. The magnetocaloric adiabatic temperature change value calculated by indirect method was 5.6 K and 5.2 K for the non-lacunar and Ca-vacancy compound, respectively. The Ca-lacunar La0.5Ca0.5-x xMnO3 (x=0.05) reported in this work demonstrated overall enhancement of the magnetocaloric effect over the LCMO. The technique used to elaborate LCMO materials was beneficial to enhance the magnetocaloric effect and magnetic behaviour. Therefore, we conclude that this less costly environmentally friendly system can be considered as more advantageous candidate for magnetic refrigeration applications then the commonly Gd-based compounds.
Materials Science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the structure, magnetic and magnetocaloric properties of La0.5Ca0.5 - x□xMnO3 (LCMO) nanocrystalline manganates by introducing calcium vacancies (Ca - vacancies) and using the sucrose - assisted auto - combustion method. Specifically, the author hopes to explore the following aspects: 1. **Structural characteristics**: Use X - ray diffraction (XRD) and the Rietveld refinement method to confirm whether the crystal structure of LCMO nanomaterials is a single - phase orthorhombic system, and analyze the influence of Ca vacancies on structural parameters. 2. **Magnetic behavior**: Study the influence of Ca vacancies on the magnetic susceptibility and magnetic transition temperature (Curie temperature) of the sample, especially the observed phase transition from paramagnetic to ferromagnetic. 3. **Magnetocaloric effect**: Evaluate the magnetic entropy change ($\Delta S_M$) and adiabatic temperature rise ($\Delta T_{ad}$) of different samples under the change of magnetic field to determine their potential as magnetic refrigeration materials. ### Formula Explanation - **Magnetic Entropy Change Formula**: \[ \Delta S_M = -\int_{H_1}^{H_2} \left(\frac{\partial M}{\partial T}\right)_H dH \] Here, $\Delta S_M$ is the magnetic entropy change, $H_1$ and $H_2$ are the applied magnetic field intensity ranges, $M$ is the magnetization intensity, and $T$ is the temperature. - **Adiabatic Temperature Rise Formula**: \[ \Delta T_{ad} = -T \int_{H_1}^{H_2} \left(\frac{\partial M}{\partial T}\right)_H \frac{dH}{C_p} \] Here, $\Delta T_{ad}$ is the adiabatic temperature rise, and $C_p$ is the specific heat capacity. ### Conclusion Through the experimental results, the author found that Ca vacancies significantly enhance the magnetocaloric effect and magnetization intensity of LCMO materials. Especially under a 6T magnetic field, the maximum entropy change of the Ca - vacancy sample is 2.70 J kg⁻¹K⁻¹, which is higher than 2.30 J kg⁻¹K⁻¹ of the non - vacancy sample. In addition, the relative cooling power (RCP) of the Ca - vacancy sample has also been improved, making it a more potential magnetic refrigeration candidate material. In summary, this study shows that by introducing Ca vacancies and using the environmentally friendly and low - cost sucrose - assisted auto - combustion method, the magnetocaloric properties of LCMO materials can be effectively improved, thus providing a new choice for magnetic refrigeration applications.