Structural and magnetic properties of $La_{0.67}Ca_{0.33}MnO_3$ (D = Ca, Sr, Ba) manganites prepared by Ball milling

Sami Mahmood,Haneen Badran,Eman Al-Hwaitat,Ibrahim Bsoul,Rola bqaeen

DOI: https://doi.org/10.48550/arXiv.1906.00407

2019-06-02

Abstract:In this research, we report on the synthesis and characterization of $La_{0.67}Ca_{0.33}MnO_3$ (LCMO), $La_{0.67}Ba_{0.33}MnO_3$ (LBMO), and $La_{0.67}Sr_{0.33}MnO_3$ (LSMO) perovskites. Precursor powders for the perovskite samples were prepared using ball mailing technique. The resulting powder was pressed into disks which were subsequently sintered at 1000 C for 2h. The structural characteristics of the prepared samples were investigated using X-ray diffraction (XRD) and scanning electron microscope (SEM), and the magnetic properties were investigated using vibrating sample magnetometry (VSM). XRD pattern of LCMO sample revealed a pure perovskite phase with Pnma space group, while the pattern of LSMO sample revealed a pure perovskite with R3c$^-$ space group. XRD pattern of LBMO sample, however, demonstrated the presence of a major perovskite phase with R3c$^-$ symmetry, together with a secondary $BaMnO_3$ phase. This secondary phase disappeared upon sintering LBMO at a higher temperature of 1100 C. Isothermal magnetic measurements and thermomagnetic curves revealed that LCMO was paramagnetic at room temperature. However, LSMO exhibited soft ferromagnetic behavior at room temperature, with Tc = 380 K and Ms = 50.9 emu/g. Also, LBMO sample sintered at 1000 C exhibited soft ferromagnetic behavior at room temperature, with Curie temperature Tc = 343 K and a rather low saturation magnetization of Ms = 30.7 emu/g. The higher sintering temperature of LBMO compound resulted in a significant increase of the saturation magnetization to 50.8 emu/g for the sample sintered at 1100 C.

Materials Science

What problem does this paper attempt to address?

The problems that this paper attempts to solve mainly focus on the following aspects:

1. **Synthesis Methods and Structural Properties**: Research on the structural properties of La0.67D0.33MnO3 (D = Ca, Sr, Ba) manganate perovskite materials prepared by high - energy ball milling and sintering at different temperatures. In particular, pay attention to the phase purity of these materials under different synthesis conditions, such as the structural changes of La0.67Ba0.33MnO3 (LBMO) samples under sintering conditions at 1000 °C and 1100 °C.

2. **Magnetic Properties**: Explore the magnetic properties of these materials, especially their magnetic behavior at room temperature. It is found that La0.67Ca0.33MnO3 (LCMO) exhibits paramagnetism at room temperature, while La0.67Sr0.33MnO3 (LSMO) and La0.67Ba0.33MnO3 (LBMO) show soft ferromagnetism, and the saturation magnetization of LBMO increases significantly with the increase of sintering temperature.

3. **Curie Temperature**: Determine the Curie temperature (Tc) of these materials by thermomagnetic measurement to understand the transition temperature from the ferromagnetic state to the paramagnetic state. It is found that the Curie temperature of LSMO is 380 K, and that of LBMO is 343 K. These results are basically consistent with the reports in the literature.

4. **Magnetocrystalline Anisotropy**: Analyze the magnetocrystalline anisotropy constant (K1) of these materials to understand the microscopic mechanism of their magnetic properties. It is found that the K1 values of LSMO and LBMO are very close, indicating that Ba and Sr have similar effects on the structure and magnetic properties of these perovskite manganates.

In summary, the main purpose of this paper is to reveal the influence of different divalent ion doping on the structure and magnetic properties of La0.67D0.33MnO3 perovskite materials through systematic experimental research, especially to explore the significant influence of sintering temperature on the structure and magnetic properties of LBMO samples.