Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Temperature Dependence of a Width of $Δ$H = $Δ$B Region in 5 wt.\% (Fe, Ti) Paticle-Doped MgB$_2$ Superconductor

Linear temperature dependence of lower critical field in<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" display="inline"><mml:mrow><mml:msub><mml:mrow><mml:mi mathvariant="normal">MgB</mml:mi></mml:mrow><mml:mrow><mml:mn>2</mml:mn></mml:mrow></mml:msub></mml:mrow></mml:math>

Linear Temperature Dependence Of Lower Critical Field In Mgb2

Superconducting Transition Width under Magnetic Field in Mgb2 Polycrystalline Samples

Thickness Dependenceof Superconducting Properties of MgB2 THIN FILMS on Al2O3 Substrates

Effect of Co Doping on Superconductivity and Transport Properties in SmFe$_{1-x}$Co$_{x}$AsO

Effect of Nano Scale Fe Doping on Superconducting Properties of MgB2

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Effect of addition of nanoparticle TiO2/SiO2 on the superconducting properties of MgB2

Superconducting Diamagnetic Fluctuations in MgB2

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

Upper Critical Fields Well above 100 T for the Superconductorsmfeaso0.85f0.15withtc

Study of high temperature resistivity and thermal stability of superconductor MgB2

Field Dependence of Π-Band Superconducting Gap in MgB 2 Thin Films from Point-Contact Spectroscopy

The doping effect of multiwall carbon nanotube on MgB2/Fe superconductor wire

Temperature Dependence of the Lower Critical Field Hc1 in Smfeaso(0.9)F(0.1) and Ba0.6k0.4fe2as2 Iron-Arsenide Superconductors

Suppression Of Superconducting Critical Current Density By Small Flux Jumps In Mgb2 Thin Films

Evolution of the pseudogap temperature dependence in YBa2Cu3O7–δ films under the influence of a magnetic field

Quantum Size Effects in Thermodynamic Superconducting Properties of Ultrathin Films

Pinning Mechanism in Carbon Nanotube Doping of Mgb2 Superconductor

Temperature dependence and limiting mechanisms of the upper critical field of FeSe thin films