Anomalous Hall effect in non-collinear antiferromagnetic antiperovskite Mn$_{3}$Ni$_{1-x}$Cu$_{x}$N

K. Zhao,T. Hajiri,H. Chen,R. Miki,H. Asano,P. Gegenwart

DOI: https://doi.org/10.1103/PhysRevB.100.045109

2019-04-11

Abstract:We report the anomalous Hall effect (AHE) in antiperovskite Mn$_{3}$NiN with substantial doping of Cu on the Ni site (i.e. Mn$_{3}$Ni$_{1-x}$Cu$_{x}$N), which stabilizes a noncollinear antiferromagnetic (AFM) order compatible with the AHE. Observed on both sintered polycrystalline pieces and single crystalline films, the AHE does not scale with the net magnetization, contrary to the conventional ferromagnetic case. The existence of the AHE is explained through symmetry analysis based on the $\Gamma_{\rm 4g}$ AFM order in Cu doped Mn$_{3}$NiN. DFT calculations of the intrinsic contribution to the AHE reveal the non-vanishing Berry curvature in momentum space due to the noncollinear magnetic order. Combined with other attractive properties, antiperovskite Mn$_{3}$AN system offers great potential in AFM spintronics.

Strongly Correlated Electrons,Materials Science,Superconductivity

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: the anomalous Hall effect (AHE) observed in the non - collinear antiferromagnetic anti - perovskite material Mn₃Ni₁₋ₓCuₓN. Specifically, the authors explored the stabilization of the non - collinear antiferromagnetic ordered structure by introducing Cu to replace Ni in Mn₃NiN and studied whether this structure can support the anomalous Hall effect.

### Problem Background

1. **Traditional View**: According to the traditional understanding, the anomalous Hall effect (AHE) is usually proportional to the net magnetization and should disappear in antiferromagnets.
2. **New Discovery**: Recent research shows that the existence of AHE is mainly determined by symmetry rather than directly related to magnetization. Some non - collinear antiferromagnets (such as hexagonal Mn₃Sn/Ge and cubic Mn₃Ir/Pt) have already demonstrated significant AHE.
3. **Material Selection**: The anti - perovskite manganese nitride Mn₃AN has attracted wide attention due to its unique physical properties (such as large negative thermal expansion, temperature - independent resistivity, etc.). These materials can form a non - collinear antiferromagnetic ordered structure at low temperatures, similar to the known AHE antiferromagnets.

### Research Objectives

- **Verify the Existence of AHE**: After introducing Cu to replace Ni in Mn₃NiN, can it stabilize the non - collinear antiferromagnetic ordered structure and exhibit AHE?
- **Explore the Mechanism**: Through experimental and theoretical calculations (such as DFT), explain why Cu - doped Mn₃NiN can exhibit AHE without depending on the net magnetization.
- **Application Potential**: Evaluate the potential application value of this material in spintronics, especially the spintronic devices based on antiferromagnets.

### Main Findings

- **Experimental Results**: In Cu - doped Mn₃NiN, significant AHE was indeed observed and did not change with the net magnetization. This phenomenon has been confirmed in both polycrystalline samples and single - crystal films.
- **Theoretical Support**: Through DFT calculations, the non - zero Berry curvature in momentum space due to non - collinear magnetic order was revealed, which provides a theoretical basis for AHE.
- **Phase Diagram Analysis**: Cu doping not only reduces the AFM transition temperature but also enhances AHE, making it more robust at lower temperatures.

### Conclusion

This study shows that Cu - doped Mn₃NiN is a new material with a non - collinear antiferromagnetic ordered structure and can exhibit significant AHE at room temperature. This finding opens up new avenues for the application of antiferromagnetic spintronics, especially having an advantage in the preparation of multilayer devices.

### Formula Examples

- **Curie - Weiss Formula**:
\[
\chi(T)=\frac{C}{T - \theta}
\]
where \(\chi(T)\) is the susceptibility, \(C\) is the Curie constant, and \(\theta\) is the Curie - Weiss temperature.

- **Berry Curvature**:
\[
\Omega_{\mathbf{k}}=\mathbf{i}\sum_{n\neq m}\frac{\langle u_m|\nabla_{\mathbf{k}}H|u_n\rangle\times\langle u_n|\nabla_{\mathbf{k}}H|u_m\rangle}{(E_m - E_n)^2}
\]
where \(\Omega_{\mathbf{k}}\) is the Berry curvature in momentum space, \(H\) is the Hamiltonian, \(u_n\) and \(u_m\) are wave functions, and \(E_m\) and \(E_n\) are energy eigenvalues.

Through these studies, the authors have successfully demonstrated the great potential of Cu - doped Mn₃NiN in the field of antiferromagnetic spintronics.