Synthesis, crystal growth and characterization of the pyrochlore Er2Ti2O7

Q. Wang,A. Ghasemi,A. Scheie,S.M. Koohpayeh
DOI: https://doi.org/10.48550/arXiv.1812.05472
2018-12-13
Abstract:Pyrochlore erbium titanate samples in the form of powders (with nominal compositions of Er2Ti2+xO7) and bulk single crystals were prepared to elucidate the effect of synthesis and growth conditions on their composition, structure, and transition temperature. All samples were characterized using X-ray diffraction and specific heat measurements. Larger lattice parameters were measured for the Ti-deficient stuffed powders, Er2(Ti2-xErx)O7-{\delta}, while Ti-rich anti-stuffed powders, (Er2-xTix)Ti2O7+{\delta}, showed a decrease in lattice parameter. The lattice parameter for the stoichiometrically synthesized powder, Er2Ti2O7, was measured to be a = 10.07522(9) Å. Single crystals grown by the conventional floating zone (FZ) technique were Ti deficient (stuffed) and darker in color due to oxygen vacancies. Using the traveling solvent floating zone (TSFZ), a high structural quality, transparent and stoichiometric Er2Ti2O7 single crystal was grown at a lower temperature using the TiO2 solvent. Heat capacity measurements of the TSFZ grown Er2Ti2O7 crystal and stoichiometric powder exhibited a very close magnetic transition temperature TC ~1.23K that was suppressed in off-stoichiometric samples, demonstrating correlations between stoichiometry and ground state magnetism in Er2Ti2O7.
Materials Science
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects: 1. **Influence of synthesis conditions on the structure and properties of Er₂Ti₂O₇**: - Research the influence of different synthesis conditions (such as powder synthesis and single - crystal growth) on the composition, structure, and transition temperature of Er₂Ti₂O₇. - Through systematic research, explore how synthesis conditions affect the stoichiometry and physical properties of the material. 2. **Relationship between stoichiometry and magnetic transition temperature**: - Explore how the enrichment or deficiency of titanium (Ti) in Er₂Ti₂O₇ samples (i.e., the change in stoichiometry) affects its lattice parameters and magnetic transition temperature \(T_C\). - Pay special attention to the inhibitory effect of the deviation from stoichiometry on the magnetic transition temperature at low temperatures. 3. **Growth of high - quality single crystals**: - Solve the problems encountered in growing single crystals by the traditional floating - zone method (FZ), such as the darkening of the crystal color and the presence of oxygen vacancies. - Successfully grow Er₂Ti₂O₇ single crystals with high crystallization quality and accurate stoichiometry using the improved traveling - solvent floating - zone method (TSFZ). 4. **Influence of defects on physical properties**: - Research the influence of defects (such as filling and anti - filling) on the bulk properties (such as heat capacity) of Er₂Ti₂O₇. - Verify that samples with accurate stoichiometry have a higher magnetic transition temperature, and the quenching disorder in these samples has a significant impact on the ground - state magnetism. ### Specific problem analysis - **Influence of stoichiometry on structure**: Through X - ray diffraction (XRD) and Rietveld refinement, it is found that Ti - deficient powder samples (\(x < 0\)) exhibit larger lattice parameters, while Ti - enriched powder samples (\(x>0\)) exhibit smaller lattice parameters. This indicates that the change in Ti content directly affects the structure of the material. - **Growth of high - quality single crystals**: Single crystals grown by the traditional FZ method have problems of Ti deficiency and oxygen vacancies, resulting in larger lattice parameters and darker color. Using the TSFZ technique, transparent single crystals with accurate stoichiometry are successfully grown at a lower temperature, verifying the effectiveness of this method. - **Research on magnetic transition temperature**: Through low - temperature specific heat measurement, it is found that the magnetic transition temperature \(T_C\approx1.23 \, \text{K}\) for TSFZ single - crystal and powder samples with accurate stoichiometry, while samples with deviated stoichiometry exhibit a lower \(T_C\). This indicates that stoichiometry has an important influence on the magnetic transition temperature. In summary, this paper aims to reveal the profound influence of synthesis conditions and stoichiometry on the structure and magnetic properties of Er₂Ti₂O₇ through systematic research, and develop an effective single - crystal growth method to obtain high - quality Er₂Ti₂O₇ single crystals.