Oxygen Pressure Modulated Magnetism and Magnetic Anisotropy of Epitaxial Transparent Yb2Ti2O7 Pyrochlore Films
Ming -Yuan Yan,Zhen-Tao Pang,Zhao-Cai Wang,Zhong-Nan Xi,Li Da Chen,Xiao-Yu Zhang,Yu-Qi Wang,Ren-Kui Zheng,Yu Deng,Shan -Tao Zhang
DOI: https://doi.org/10.1103/physrevb.108.094105
IF: 3.7
2023-01-01
Physical Review B
Abstract:Pyrochlore Yb2Ti2O7 has gained significant attention due to the low-temperature geometrical frustration induced unusual magnetic phase. Most experimental studies on Yb2Ti2O7 have been performed on polycrystalline bulk or single crystals; however, there have been a few reports detailing the structure and magnetism of Yb2Ti2O7 thin films. Here, we fabricated high-quality (001)-, (110)-, and (111)-epitaxial transparent Yb2Ti2O7 films on single-crystal yttria-stabilized ZrO2 (YSZ) substrates with various oxygen pressures by pulsed laser deposition. Structural characterizations confirm flat surface and uniform and well-defined atomic arrangement of the Yb2Ti2O7 films, as well as atomic-scale epitaxial and sharp Yb2Ti2O7/YSZ interface. The (111) oriented films fabricated at 10 Pa oxygen pressure have the highest magnetization value of 2.03 mu B/Yb, which is higher than that of bulk counterparts, due to the fact that the distorted Yb-tetrahedra induced by interfacial strain and defects can destroy magnetic frustration and enhance magnetization. Especially, the fabricated (001)-, (110)-, and (111)-epitaxial Yb2Ti2O7 films illustrate a significantly pronounced magnetic anisotropy, which results from the single ion anisotropy of Yb and the anisotropic exchange interactions. In addition, a wide-spectrum transmittance of similar to 95% was achieved in (110)-epitaxial Yb2Ti2O7 films, which is comparable to the state-of-the-art transparent materials. Our work gives a comprehensive perspective on the structure, magnetism, magnetic anisotropy, and transmittance of Yb2Ti2O7 films, which may guide further work on pyrochlore materials.