Abstract:The control of the morphology of nanoparticles is a hot issue all over the world.Organic-inorganic materials can be tailor made with an infinite number of architectures and in diverse forms conveniently.A new type of organic inorganic hybrid material was reported to be synthesized by emulsion polymerization by using the monomers which contained alkoxysilane groups.However,polymerization and morphology could hardly be controled during the emulsion process, because the alkoxysilane group was easy to be subjected to hydrolysis and condensation by sol gel process which decreased the stability of the latex.In the present work, organic inorganic hybrid core shell nanoparticles were synthesized by seeded emulsion polymerization.Through morphology design, polystyrene, as seeded cores, was synthesized firstly, then 3 trimethoxysilyl propyl methacrylate (MPS) was added to form MPS styrene copolymer shell on the surface of polystyrene core. Owing to the hydrolysis condensation of organic alkoxysilane groups in MPS,the organic inorganic hybrid shell was formed through sol gel process.The core shell structure was interpreted by thermodynamical representation and characterized by transmission electron microscopy (TEM).The nonionic surfactant used would decrease the stability of the latex.In acidic condition the latex turned into gel just after the addition of MPS,while,in basic condition the particle number decreased obviously, and the latex kept almost stable in neutral condition.The higher the MPS concentration in the emulsion was,the less stability the latex had.Adding MPS continuously could keep the latex more stable and the particle size could be controlled by this method.Then, the core of this kind of hybrid nanoparticles could be dissolved to yield hollow nanocapsules, with the proportion of the void volume 40 1%.

Enhanced stability and bioconjugation of photo-cross-linked polystyrene-shell, Au-core nanoparticles

Amphiphilic multiblock copolymer stabilized Au nanoparticles

Synthesis of the Supported Au Polystyrene/poly (acrylic acid) Composite Microspheres and Their pH Regulated Performance

Enhanced stability of gold nanoparticles capped with double hydrophilic block copolymers synthesized by eATRP

Facile Synthesis of Crosslinked Core/Shell Silver Nanoparticles with Significantly Improved Thermal Stability

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Double hydrophilic block copolymer monolayer protected hybrid gold nanoparticles and their shell cross-linking.

Plasmon-enhanced Luminescence in Novel Complex Conjugated Polymer Nanoparticles.

Enhanced Stability Of Core-Surface Cross-Linked Micelles Fabricated From Amphiphilic Brush Copolymers

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control

The High Yield Synthesis and Characterization of Gold Nanoparticles with Superior Stability and Their Catalytic Activity

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Multidentate Zwitterionic Chitosan Oligosaccharide Modified Gold Nanoparticles: Stability, Biocompatibility and Cell Interactions

Facile and controlled fabrication of functional gold nanoparticle-coated polystyrene composite particle

Platinum-nanoparticle-supported core–shell polymer nanospheres with unexpected water stability and facile further modification

Copolymer-Coated Gold Nanoparticles: Enhanced Stability and Customizable Functionalization for Biological Assays

Synthesis and Structural Control of Gold Nanoparticles-Coated Polystyrene Composite Particles Based on Colloid Thermodynamics

Effect of Thermo‐ and pH‐sensitive Block Copolymer Structure and Composition on the Synthesis and Stabilization of Gold Nanoparticles

Preparation of Functionalized Core‐Shell Alumina/Polystyrene Composite Nanoparticles, 1

Gold Nanoparticles Coated with Polysarcosine Brushes to Enhance Their Colloidal Stability and Circulation Time in Vivo.