Abstract:A novel in situ autoreduction route has been developed, by which monodispersed silver nanoparticles with tunable sizes could be easily fabricated on silica-based materials, especially inside the channels of mesoporous silica (MPS). 13C CP/MAS NMR spectroscopy was employed to monitor the whole assembly process. It was demonstrated that the amino groups of APTS (aminopropyltriethoxyl silane)-modified MPS can be used to anchor formaldehyde to form novel reducing species (NHCH2OH), on which Ag(NH3)2NO3 could be in situ reduced. Monodispersed silver nanoparticles were thus obtained. In situ XRD and in situ TEM experiments were used to investigate and compare the thermal stabilities of silver nanoparticles on the external surface of silica gels (unconfined) and those located inside the channels of SBA-15 (confined). It was observed that unconfined silver nanoparticles tended to agglomerate at low temperatures (i.e., lower than 773 K). The aggregation of silver nanoparticles became more serious at 773 K. However, for those confined silver nanoparticles, no coarsening process was observed at 773 K, much higher than its Tammann temperature (i.e., 617 K). Only when the treating temperature was higher than 873 K could the agglomeration of those confined silver nanoparticles happen with time-varying via the Ostwald ripening process. The confinement of mesopores played a key role in improving the thermal stabilities of silver nanoparticles (stable up to 773 K without any observable coarsening), which is essential to the further investigations on their chemical (e.g., catalytic) properties.

Facile Synthesis of Crosslinked Core/Shell Silver Nanoparticles with Significantly Improved Thermal Stability

Thermoresponsive Polymer-Stabilized Silver Nanoparticles

A Facile Method to Synthesize PS/Ag Composite Micro-spheres

A Facile Synthetic Route to Aqueous Dispersions of Silver Nanoparticles

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

The optimization of methods of synthesis of nickel–silver core–shell nanoparticles for conductive materials

Silver-nickel Oxide Core-Shell Nanoparticle Array Electrode with Enhanced Lithium-Storage Performance

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Fabrication Of Fully Covered Cu-Ag Core-Shell Nanoparticles By Compound Method And Anti-Oxidation Performance

Facile Synthesis of Polymer Core@silver Shell Hybrid Nanoparticles with Super Surface Enhanced Raman Scattering Capability

Enhanced thermal stability of monodispersed silver cluster arrays assembled on block copolymer scaffolds

Fabrication and characterization of silver core and porous silica shell nanocomposite particles

Platinum-nanoparticle-supported core–shell polymer nanospheres with unexpected water stability and facile further modification

Preparation and study of polyacryamide-stabilized silver nanoparticles through a one-pot process.

Chemical Synthesis of Silver Nanoparticles Using Tri-sodium Citrate, Stability Study and Their Characterization

Towards understanding the facile synthesis of well-covered Cu-Ag core-shell nanoparticles from a complexing model

A Facile Synthesis of Silver-Coated Composite Particles by Swelling Surface Method

Carbon‐Assisted Stable Silver Nanostructures

Rapid Synthesis of High-Stable Silver Nanoparticles by Electrochemical Method

Stability evolution of ultrafine Ag nanoparticles prepared by laser ablation in liquids

Synthesis of Silver Nanoparticle-Coated Poly(styrene-Co-sulfonic Acid) Hybrid Materials and Their Application in Surface-Enhanced Raman Scattering (SERS) Tags