Shrinkage and strength characterization of an alumina-glass interpenetrating phase composite for dental use

Hang Wang,Yunmao Liao,Yonglie Chao,Xing Liang

DOI: https://doi.org/10.1016/j.dental.2006.06.041

Abstract:Objective: The aim of the study was to investigate the influence of temperature and time during partial-sintering (i.e. initial-stage sintering) on the shrinkage and strength of an alumina-glass dental composite. Methods: The alumina slip and infiltrating glass were prepared for fabrication of an interpenetrating phase composite by melt-infiltration technology. Partial-sintering temperatures for the alumina body ranged from 1050 to 1200 degrees C (2 h) and at 1125 degrees C, the time was varied from 2 to 8 h. Partially sintered alumina preform were then infiltrated with melted glass at 1125 degrees C for 6h except for one group treated at 1100 degrees C for 6 h. Result: The composite demonstrated shrinkage not only during initial-stage sintering of the alumina but also during infiltration of glass into the alumina preform. Higher temperatures and longer times for alumina sintering led to greater shrinkage for the alumina preform and overall for the alumina-glass infiltrated composite. However, shrinkage during the infiltration stage was lower for alumina compacts having the highest initial-stage sintering shrinkage (1200 degrees C for 2 h or at 1125 degrees C for 6 and 8 h). Strength of the composite was not influenced when sintering temperatures and times were increased. Significance: Shrinkage during both alumina sintering and glass infiltration must be taken into account for the overall shrinkage of the alumina-glass interpenetrating phase composite. Strength does not appear to be influenced by the changes in density or preform microstructure occurring during more extensive initial-stage sintering.