Influence of Fe-doping amounts on magnetocaloric properties of Gd-based amorphous microfibers
Jingshun Liu,Guanda Qu,Xufeng Wang,Hongneng Chen,Yun Zhang,Guanyu Cao,Rui Liu,Sida Jiang,Hongxian Shen,Jianfei Sun
DOI: https://doi.org/10.1016/j.jallcom.2020.156190
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>The effects of trace Fe-doping on the magnetic and magnetocaloric performances of Gd-based metallic microfibers were systematically and detailedly investigated in this article. Experimental results indicated that the Gd-based microfibers prepared by the rotated-dipping process are uniform and continuous, with typically amorphous structure characteristics and favorable thermal stability. Curie temperature <em>T</em><sub>C</sub> of Gd-based amorphous microfibers increases with the rising of Fe content, and the <em>T</em><sub>C</sub> of GdAlCoFe3 microfibers is the highest at 128.7 K (relatively increased by 15.3 K than before doping). Among the general magnetic performance indicators, the saturation magnetization <em>M</em><sub>s</sub> of GdAlCoFe2 microfibers reaches a peak at 264.04 emu/g. Furthermore, the values of magnetocaloric performance indexes of Gd-based amorphous microfibers increase firstly and then decrease with the rising of Fe-doping amount. When the external magnetic field <em>H</em><sub>ex</sub> = 50,000 Oe, the maximum magnetic entropy change -Δ<em>S</em><sub>m</sub><sup>max</sup>, refrigeration capacity <em>RC</em> and relative cooling power <em>RCP</em> of GdAlCoFe1 microfibers are 10.33 J/kg·K, 748.22 J/kg and 1006.90 J/kg, which increased by 0.07 times, 0.13 times and 0.16 times, respectively than before Fe-doping (namely -Δ<em>S</em><sub>m</sub><sup>max</sup> = 9.68 J/kg·K, <em>RC</em> = 663.79 J/kg, <em>RCP</em> = 871.73 J/kg). From the perspective of microstructural changes, Fe-doping results in the formation tendency of atomic clusters and nanocrystals in micro-regions, the orderly orientation of atoms appears, and the magnetic anisotropy increases accordingly. In addition, the 3d electron layer of the doped Fe element in Gd-Al-Co-Fe quaternary alloy system enhances the RKKY indirectly exchange coupling interaction and changes the state of magnetic entropy, which in turn leads to an increase in Curie temperature and an improvement in magnetocaloric performance. Since <em>RC</em> and <em>RCP</em> are the main indicators in engineering applications, the GdAlCoFe1 amorphous microfibers can be selected as a low-temperature magnetic refrigeration working medium to provide technical guarantee for the application of magnetic refrigeration technology.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering