Effect of current annealing treatment on magnetic properties of Gd-Al-Co-Fe metallic microfibers
Jingshun Liu,Meifang Huang,Mengjun Wu,Yun Zhang,Guanyu Cao,Ze Li,Hongneng Chen,Tianchi Yu,Xufeng Wang,Rui Liu,Guanda Qu,Mengyao Pang,Hongxian Shen
DOI: https://doi.org/10.1016/j.jallcom.2020.157231
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>Herein, the influence of annealing current intensities on magnetic properties of Gd-based microfibers was systematically investigated. The experimental results indicated that the as-prepared microfibers have amorphous structure and excellent thermal-stability, and the Curie temperature <em>T</em><sub>C</sub> of which slightly change before and after annealing. The general magnetic physical magnitudes (<em>M</em><sub>s</sub>, <em>M</em><sub>r</sub>, <em>μ</em><sub>0</sub><em>H</em><sub>c</sub> and <em>μ</em><sub>m</sub>) of microfibers increase firstly and then decrease with the rising of annealing current intensities, and those of the microfibers annealed at 90 mA microfibers are more obvious (<em>M</em><sub>s</sub> = 255 A m<sup>2</sup>/kg and <em>μ</em><sub>m</sub> = 0.38 ± 0.01). Similarly, the magnetocaloric parameters of microfibers also increase firstly and then decrease with the rising of current intensities. At 5 T of magnetic field change <em>μ</em><sub>0</sub>Δ<em>H</em>, the maximum magnetic entropy change Δ<em>S</em><sub>m</sub><sup>max</sup> and refrigerant capacity <em>RC</em> of 90 mA annealed metallic microfibers are 12.77 J/(kg·K) and 906 J/kg, respectively, and which remarkably increased in compared with the as-prepared state, respectively. From the microstructural evolution perspective, a certain intensity current annealing induces the tendency of micro-regional clusters and nanocrystals, forming atomic ordered regions, and the internal residual stress release with a reduction of magnetic anisotropy. Meanwhile, the magnetic ordering and the critical magnetic-moment rotational driving-force were changed after Fe-doping, resulting in effective improvement of refrigerant capacity. Accordingly, the current-annealed Gd-Al-Co-Fe microfibers can be adopted as low-temperature magnetic refrigeration working-medium, which also provides a theoretical foundation for magnetic refrigeration technology application.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering