Abstract:In fusion reactors, plasma-facing materials will be exposed to low-energy and high-flux plasma of the hydrogen isotopes fuel, i.e., deuterium (D) and tritium (T), along with helium (He), the product of nuclear fusion reactions. He irradiation is likely to trigger the formation of He bubbles beneath the material surface, exerting complex effects on the migration patterns of hydrogen isotopes. In this work, molecular dynamics simulations were employed to investigate the influence of nano-sized He bubbles on the D migration behavior in tungsten (W) during the continuous implantation and diffusion processes, which is more consistent with the fusion environment for plasma-facing materials. It is found that the influence of He bubbles on D migration behavior can be classified into barrier and trapping effects. These effects show a competitive relationship at different processes. During the implantation process, the barrier effect takes precedence over the trapping effect, leading to the reduced D retention. Conversely, during the diffusion process, the trapping effect dominates over the barrier effect, resulting in increased D retention. Due to the surface of He bubbles serves as the trapping sites for hydrogen isotopes, augmenting the size and density of He bubbles notably enriches the strong trapping sites in W. When the location of He bubble is closer to the surface, a higher frequency of interaction events occurs between the implanted D atoms and He bubbles, consequently increasing D retention. Additionally, it was also found that the lattice distortion in pure W is more pronounced than that in He bubble-containing W at high temperatures due to the robust interaction between D and He, which diminishes collisions between D atoms and the W lattice. This study gives a valuable insight into the influence of He bubbles on hydrogen isotopes migration behavior in the fusion environment.

The effect of W fuzz growth on D retention in polycrystalline W

Modeling D Retention in W under D Ions and Neutrons Irradiation

Deuterium Gas-Driven Permeation and Retention in ZrC Dispersion-Strengthened W and Pure W

Competitive Barrier and Trapping Effects of Helium Bubbles on Hydrogen Isotopes Migration Behavior in Tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Studies on the impacts of the pore size and shape on deuterium retention in tungsten fuzzy nanostructures

Irradiation hardening and deuterium retention behaviour of tungsten under synergistic irradiations of 3.5 MeV Fe 13+ ions and deuterium plasma

Tungsten fuzz annealing effect on deuterium retention in polycrystalline tungsten

Hydrogen Trapping under the Effect of W–C Mixed Layers

Hydrogen retention and affecting factors in rolled tungsten: Thermal desorption spectra and molecular dynamics simulations

Effect of Grain Size on the Behavior of Hydrogen/helium Retention in Tungsten: a Cluster Dynamics Modeling

The effect of Ar+ impurity on W nano-fuzz growth over polycrystalline W targets

Influence of radiation defects on deuterium permeation behavior in tungsten

Deuterium Retention in Heavy-Ion and Helium-Ion Sequentially Irradiated Tungsten

Reduced D Trapping by Plasma-Implanted He Nanobubbles in Radiation Damaged Tungsten

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Deuterium retention in tungsten and tungsten alloys exposed to pure and impurities seeding deuterium plasma

Influence of Surface Melting on the Deuterium Retention in Pure and Lanthanum Oxide Doped Tungsten

Characterization on deuterium retention in tungsten target using spatially resolved laser induced desorption-quadrupole mass spectroscopy

Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma