Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

A new method to synthesize nickel carbide (Ni3C) nanoparticles in solution

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Facile synthesis of a metastable nanocrystalline Ni3N from nickel nanoparticle

A Novel Sol–gel Process to Facilely Synthesize Ni3Fe Nanoalloy Nanoparticles Supported with Carbon and Silica

In situ flame synthesis of polyhedral nickel oxide nanoparticles on carbon fibers

Factors affecting formation of metastable Ni 3C phase in a solution-based method

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Factors Affecting Formation of Metastable Ni<sub>3</sub>C Phase in a Solution-Based Method

Nickel Carbide (Ni3C) Nanoparticles for Catalytic Hydrogenation of Model Compounds in Solvent

Controllable preparation of Ni nanoparticles for catalysis of coiled carbon fibers growth.

Simple Synthesis and Characterization of Shell-Thickness-Controlled Ni/Ni3C Core-Shell Nanoparticles

Synthesis Of Nickel Nanoparticles And Carbon Encapsulated Nickel Nanoparticles Supported On Carbon Nanotubes

Large Scale Synthesis and Characterization of Ni Nanoparticles by Solution Reduction Method

The Efficient Synthesis of Carbon Nano-Onions Using Chemical Vapor Deposition on an Unsupported Ni–Fe Alloy Catalyst

Facile fabrication of ultrafine CoNi alloy nanoparticles supported on hexagonal N-doped carbon/Al2O3 nanosheets for efficient protein adsorption and catalysis

Synthesis of carbon coated nano Fe-Ni magnetic particles | (Chinese Source)

Synthesis of Carbon Coated Nano Fe-Ni Magnetic Particles

Controllable Synthesis of Hexagonal Close-Packed Nickel Nanoparticles under High Nickel Concentration and Its Catalytic Properties