Abstract:PURPOSE:Using sandblast, double acid-etching and H(2)O(2)/HCl solution treatment to establish a new implant surface, and to analyze the surface's morphology.METHODS:After being polished, sandblasted, cleaned, the titanium specimens were divided into six groups, i.e.A to F group. The specimens of group A were treated with low concentration of HF/HNO(3) solution, Group B was treated with low concentration of HF/HNO(3) solution and then H(2)SO(4)/HCl solution, Group C was treated after Group B and further with H(2)O(2)/HCl solution at 80degrees centigrade for 30 minutes, and subsequently heated at 400degrees centigrade for 1 hour. Group D was treated with high concentration of HF/HNO(3) solution, Group E was treated after Group D and then H(2)SO(4)/HCl solution, Group F was treated after E group and further with H(2)O(2)/HCl solution at 80degrees centigrade for 30 minutes, and subsequenty heated at 400degrees centigrade for 1 hour.RESULTS:The titanium surface sandblasted and ultrasonically cleaned exhibited a great deal of particles. The titanium plates treated with low concentration of HF/HNO(3) solution still had some particles, but there were much nano-holes on the titanium surface. The titanium plates treated with high concentration of HF/HNO(3) solution had no particles on the surface, but showed much micron-holes on the titanium surface. The titanium plates treated with H(2)SO(4)/HCl solution after HF/HNO(3) solution etching had all particles removed and got multilevel holes on the surface.The last H(2)O(2)/HCl method produced an anatase titania gel layer on the specimen surface.CONCLUSION:By altering the concentration of HF/HNO(3) solution, we could make different sizes of apertures on the titanium surface. Double acid-etching can remove all sandblasting particles embedded in titanium surfaces and form multilevel holes. The H(2)O(2)/HCl method can turn the rough non- crystallographic TiO(2) layer into the anatase titania gel layer.

Surface modification of titanium by etching in concentrated sulfuric acid

Bioactive treatment of titanium surface using a H2O2/HCl solution

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

The Preparation of the Multilevel Holes and Analysis of the Pure Titanium Surface

Surface modification of titanium by anodic oxidation in phosphoric acid at low potentials. Part 2. In vitro and in vivo study

Surface modification of titanium by anodic oxidation in phosphoric acid at low potentials. Part 1. Structure, electronic properties and thickness of the anodic films

Nanopore formation on the surface oxide of commercially pure titanium grade 4 using a pulsed anodization method in sulfuric acid

Optimization and Characterization of Anatase Formed on Anodized Titanium in Sulfuric Acid

Influence of Cupric, Ferric, and Chloride on the Corrosion of Titanium in Sulfuric Acid Solutions Up to 85°C

Influence of concentration of sulfuric and hydrochloric acids on corrosion resistance of porous titanium

Bioactivity of Metallic Biomaterials with Anatase Layers Deposited in Acidic Titanium Tetrafluoride Solution

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

(Digital Presentation) Corrosion-Resistance Investigation of Titanium Passive Layer in Acidic Solution

Effects of acid-alkali treatment on bioactivity and osteoinduction of porous titanium: An in vitro study

Influence of ultrasonic shot peening on the surface acid etching behavior of pure titanium

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces

Reduction of Contact Resistance on Titanium Sheet Surfaces by Formation of Titanium Carbide and Nitride, and its Stability in Sulfuric Acid Aqueous Solution

Enhanced Bioactivity of Sandblasted and Acid-Etched Titanium Surfaces

Surface Modifications by Both Anodic Oxidation and Ion Beam Implantation on Electropolished Titanium Substrates