Drying Shrinkage and Mechanical Strength of Cementitious Composites with Alkali-Treated Makino Bamboo Fibers

Chin-Hao Yeh,Jyh-Horng Wu,Teng-Chun Yang,Chin-Hao YehJyh-Horng WuTeng-Chun YangDepartment of Forestry,National Chung Hsing University,Taichung,Taiwan

DOI: https://doi.org/10.1080/15440478.2024.2321531

2024-03-08

Journal of Natural Fibers

Abstract:Alkali-treated bamboo fibers (AFs) treated with different NaOH concentrations (5 and 10%) and treatment times (1, 12, and 24 h) were used as fillers to fabricate cementitious composites with AFs (CAFs) in the present study. The results demonstrated that alkali treatment caused the partial decomposition of hemicellulose and lignin and an increase in the surface roughness of bamboo fibers. Additionally, the amounts of calcium hydroxide in alkali-treated CAFs were higher than in untreated CAFs, and they increased with increasing NaOH concentration and treatment time. For drying shrinkage (DS) under 75% relative humidity (RH), the DS values of the CAFs significantly decreased after adding AFs compared to the DS values of untreated CAFs. Compared to untreated CAFs, the density of the 5% and 10% NaOH-treated CAFs with longer treatment times decreased by 2.9% and 5.1%, respectively. Furthermore, the tensile strength of all alkali-treated CAFs exhibited no significant differences when compared with that of untreated CAFs, while the modulus of rupture and compressive strength were significantly decreased by NaOH treatment. These results indicated that the AFs significantly improved the drying shrinkage of the CAFs and hydration retardation effect of cement pastes, while the density and mechanical strength of the CAFs decreased. 本研究采用不同NaOH浓度(5%和10%)和处理时间(1、12和24小时)的碱处理竹纤维(AF)作为填料,制备了含有AF的水泥基复合材料. 结果表明,碱处理使竹纤维的半纤维素和木质素部分分解,表面粗糙度增加. 此外,碱处理的CAFs中的氢氧化钙含量高于未处理的CAF,并且随着NaOH浓度和处理时间的增加而增加. 对于75%相对湿度(RH)下的干燥收缩率(DS),与未处理的CAFs相比,添加AF后的CAFs的DS值显著降低. 与未处理的CAFs相比,处理时间较长的5%和10%NaOH处理的CAF的密度分别降低了2.9%和5.1%. 此外,与未处理的CAFs相比,所有碱处理的CAF的拉伸强度没有显著差异,而NaOH处理显著降低了断裂模量和抗压强度. 这些结果表明,AF显著改善了CAFs的干燥收缩和水泥浆体的水化阻滞效果,同时降低了CAFs的密度和机械强度.

materials science, textiles

What problem does this paper attempt to address?

The main problem this paper attempts to address is improving the drying shrinkage rate and mechanical properties of cement-based composites (CAFs) by using alkali-treated bamboo fibers (AFs) with different concentrations and treatment times. Specifically, the researchers aim to solve the problem through the following points:

1. **Improving Drying Shrinkage Rate**: The study found that the addition of alkali-treated bamboo fibers significantly reduced the drying shrinkage rate of cement-based composites at 75% relative humidity (RH). This indicates that alkali-treated bamboo fibers can effectively reduce the drying shrinkage of cement-based composites.

2. **Optimizing Mechanical Properties**: Although the addition of alkali-treated bamboo fibers had little effect on tensile strength, it significantly reduced the modulus of rupture and compressive strength. This suggests that while alkali-treated bamboo fibers improve the drying shrinkage rate, they may reduce certain mechanical properties of the material.

3. **Understanding the Mechanism**: Using Fourier Transform Infrared Spectroscopy (FTIR), X-ray Diffraction (XRD), Thermogravimetric Analysis (TGA), and Scanning Electron Microscopy (SEM), the researchers analyzed the effects of alkali treatment on the chemical composition and microstructure of bamboo fibers in detail. The results showed that alkali treatment led to partial decomposition of hemicellulose and lignin in the bamboo fibers, increasing surface roughness, which helps improve the bonding between the fibers and the cement matrix.

4. **Exploring Optimal Conditions**: The researchers explored the optimal treatment conditions to achieve the best drying shrinkage rate and mechanical properties by using different concentrations (5% and 10%) and treatment times (1, 12, and 24 hours) of alkali treatment.

In summary, this paper aims to find an effective method to use alkali-treated bamboo fibers to improve the drying shrinkage rate of cement-based composites through systematic research, while also evaluating its impact on mechanical properties.