Preparation and mechanical properties of Portland cement composites filled with bamboo fibres modified by acetic acid and fermentation treatment

Yuanbin Li,Xia Zheng,Xingong Li

DOI: https://doi.org/10.1080/21650373.2024.2334338

2024-04-10

Journal of Sustainable Cement-Based Materials

Abstract:To improve the compatibility between Portland cement and bamboo fibre, bamboo fibres were modified by acetic acid and fermentation treatment and the modified bamboo fibres/Porland cement composites were prepared. The hydration curves of the bamboo fibres/Porland cement composites were measured and the area ratio under the cement hydration heat curve was used as the compatibility coefficient to evaluate the compatibility of bamboo fiber and cement. The hydration products at different hydration times were characterized by XRD, FTIR, and SEM. Moreover, the mechanical strengths of standard test blocks of Portland cement/bamboo fibre composites were tested to further verify the improved compatibility of bamboo fiber and Portland cement. The study shows that the compatibility between bamboo fibre and Portland cement was improved from 9% to 87%, the bending strength of Portland cement/bamboo fibre composite was increased from 638 N to 3678 N, and the compressive strength was increased from 1.5 MPa to 34.35 MPa.

construction & building technology,materials science, multidisciplinary,green & sustainable science & technology