Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Ultralow-density double-layer silica aerogel fabrication for the intact capture of cosmic dust in low-Earth orbits

Silica aerogel for capturing intact interplanetary dust particles for the Tanpopo experiment

Design of a silica-aerogel-based cosmic dust collector for the Tanpopo mission aboard the International Space Station

Tanpopo cosmic dust collector: Silica aerogel production and bacterial DNA contamination analysis

Fabrication and Properties of Optically Transparent Silica Aerogels for Hypervelocity Particle Capture

Scientific Targets of Tanpopo: Astrobiology Exposure and Micrometeoroid Capture Experiments at the Japanese Experiment Module Exposed Facility of the International Space Station

Aerogel: Space exploration applications

A Fluorescent Aerogel for Capture and Identification of Interplanetary and Interstellar Dust

Development of transparent silica aerogel over a wide range of densities

Fabrication of Silica Aerogel Micro-cylinder for Inertial Confinement Fusion Target

Production of low-density sodium silicate-based hydrophobic silica aerogel beads by a novel fast gelation process and ambient pressure drying process

Developing a silica aerogel radiator for the HELIX ring-imaging Cherenkov system

Preparation of high-strength silica aerogels by two-step surface modification via ambient pressure drying

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Rapid synthesis of sodium silicate based hydrophobic silica aerogel granules with large surface area

Ultralight Silica Foams with a Hierarchical Pore Structure Via a Surfactant-Free High Internal Phase Emulsion Process

Auto-Continuous Synthesis of Robust and Hydrophobic Silica Aerogel Microspheres from Low-Cost Aqueous Sodium Silicate for Fast Dynamic Organics Removal

Unidirectional Ice-Templating for Aerogel Adsorbents: Excellent Pore Structure and High CO2 Capture Performance for Direct Air Capture

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique