Laser powder-bed fusion additive manufacturing: physics of complex melt flow and formation mechanisms of pores, spatter and denudation zones

Saad A. Khairallah,Andrew T. Anderson,Alexander Rubenchik,Wayne E. King

DOI: https://doi.org/10.1016/j.actamat.2016.02.014

2016-01-06

Abstract:This study demonstrates the significant effect of the recoil pressure and Marangoni convection in laser powder bed fusion (L-PBF) of 316L stainless steel. A three-dimensional high fidelity powder-scale model reveals how the strong dynamical melt flow generates pore defects, material spattering (sparking), and denudation zones. The melt track is divided into three sections: a topological depression, a transition and a tail region, each being the location of specific physical effects. The inclusion of laser ray-tracing energy deposition in the powder-scale model improves over traditional volumetric energy deposition. It enables partial particle melting, which impacts pore defects in the denudation zone. Different pore formation mechanisms are observed at the edge of a scan track, at the melt pool bottom (during collapse of the pool depression), and at the end of the melt track (during laser power ramp down). Remedies to these undesirable pores are discussed. The results are validated against the experiments and the sensitivity to laser absorptivity is discussed.

Fluid Dynamics

What problem does this paper attempt to address?

This paper attempts to solve the problems of complex melt flow and defect formation mechanisms in the laser powder bed fusion (L - PBF) additive manufacturing process, especially the problems such as pores, spatters and denudation zones in 316L stainless steel during the L - PBF process. Specifically:

1. **Dynamics behavior of complex melt flow**: Through a high - fidelity three - dimensional powder - scale model, the paper reveals how strong - dynamic melt flow leads to the formation of pore defects, material spatter and denudation zones. These phenomena are difficult to accurately capture in traditional volumetric energy deposition models.

2. **Pore formation mechanisms**: It is found that different types of pores are formed at different positions of the scanning track:
- Pores formed at the edge of the scanning track.
- Pores formed when the bottom of the melt pool collapses.
- Pores formed at the tail of the melt pool (when the laser power drops).

3. **Physical mechanisms of spatter and denudation zones**: The paper explains in detail the formation mechanisms of spatter and denudation zones and proposes strategies to avoid these adverse effects. For example, laser ray - tracing energy sources and considering the role of recoil pressure are helpful to describe these physical mechanisms.

4. **Improved energy deposition model**: Compared with the traditional volumetric energy deposition model, the paper introduces the laser ray - tracing energy deposition method, which can more accurately simulate the partial particle melting phenomenon, and this has an important impact on the formation of pore defects.

5. **Experimental verification and sensitivity analysis**: The research results are verified by experiments, and the influence of laser absorptivity on the results is discussed. The experimental data show that the model has good quantitative consistency in predicting the depth and width of the melt pool.

Through the above research, the paper provides an important theoretical basis and technical support for improving the quality and reliability of the L - PBF process, especially in reducing pores and other defects.