Compression and fretting wear studies of γ/α 2 duplex TiAl alloys at the nanoscale

Min Zheng,Jianfeng Han,dingfeng Qu,Weihua Chen,Yuhang Sun,Jie Chen,Zongxiao Zhu
DOI: https://doi.org/10.1088/1402-4896/ad3ee9
2024-04-16
Physica Scripta
Abstract:The nanofabrication behavior of γ/α2 duplex TiAl alloys by downward pressure followed by reciprocating friction with investigating diamond grinding balls via MD simulation. It was found that a certain number of dislocations in the workpiece was low and the resilience was high during the initial pressing stage, and the number of dislocations increased, the resilience decreased and the plastic deformation capacity was enhanced under continuous pressing. The α2 phase did not deform significantly during the compression process. The presence of the α2 phase increases the overall hardness of the material, and elastic-plastic deformation occurs mainly where the γ phase is present, The endowment layer dislocations generated during the intrinsic stacking fault rebound via the phase boundary to form V-shaped dislocations. During the reciprocating friction of the workpiece, forward friction produces Vshaped dislocations, and reverse friction makes the dislocations disappear. This process results in the forward average friction force being greater than the reverse average friction force. γ/α2 phase boundary has an impeding effect on the downward proliferation of defects, and the existence of the phase boundary makes the temperature transfer appear discontinuous. During friction, the certain number of vacancy atoms in the γ-phase increases and the transition between FCC and HCP occurs.
physics, multidisciplinary
What problem does this paper attempt to address?