Abstract:We present electrical transport measurements in natural graphite and highly ordered pyrolytic graphite (HOPG), comparing macroscopic samples with exfoliated, nanofabricated specimens of nanometer thickness. The latter exhibit a very large c-axis resistivity $\rho_c$ -- much larger than expected from simple band theory -- and non-monotonic temperature dependence, similar to macroscopic HOPG, but in stark contrast to macroscopic natural graphite. A recent model of disorder-induced delocalization is consistent with our transport data. Furthermore, Micro-Raman spectroscopy reveals clearly reduced disorder in exfoliated samples and HOPG, as expected within the model -- therefore presenting further evidence for a novel paradigm of electronic transport in graphite.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is about the abnormal behavior of the resistivity $ \rho_c $ along the c - axis (perpendicular to the basal plane of graphite) in graphite and its temperature dependence $ \rho_c(T) $. Specifically, the researchers found: 1. **Simple band theory cannot explain the experimental results**: The traditional band structure model predicts that both the c - axis resistivity $ \rho_c $ and the in - plane resistivity $ \rho_{ab} $ of graphite should have a monotonic metallic temperature dependence, and the resistivity anisotropy $ RA=\frac{\rho_c}{\rho_{ab}} $ should remain constant at different temperatures. However, the experimentally observed results are inconsistent with these predictions. 2. **Differences in macroscopic and nanoscale samples**: Macroscopic natural graphite (NG) exhibits a weak metallic temperature dependence, while highly oriented pyrolytic graphite (HOPG) exhibits a non - monotonic temperature dependence on the macroscopic scale, especially $ \rho_c $ has a maximum at about 40 K. In addition, the resistivity anisotropy of HOPG is much larger than expected. 3. **Abnormal behavior in nanoscale samples**: The researchers prepared graphite flakes with thickness in the nanometer range by exfoliation and nanofabrication techniques and measured $ \rho_{ab} $ and $ \rho_c $ of these samples. The results show that all types of nano - graphite exhibit abnormal behavior, that is, large resistivity anisotropy and non - metallic temperature dependence, which is in sharp contrast to the behavior of macroscopic NG but similar to that of macroscopic HOPG. To understand these abnormal phenomena, the researchers introduced a new transport mechanism - disorder - induced delocalization. According to this model, the c - axis transport in weakly disordered samples is strongly suppressed due to one - dimensional Anderson localization, resulting in very large $ \rho_c $ and anisotropy $ RA $. However, when there is sufficient bulk scattering, this localization will be destroyed, thereby reducing $ \rho_c $ and $ RA $. The characterization of the disorder degree of the samples by micro - Raman spectroscopy further supports this model. Studies have shown that exfoliated samples and HOPG samples have a lower disorder degree, while macroscopic NG samples exhibit a higher disorder degree. Therefore, this paper provides experimental evidence for disorder - induced delocalization as a new paradigm for electron transport in graphite. ### Formula summary - Resistivity anisotropy: \[ RA = \frac{\rho_c}{\rho_{ab}} \] - Calculation formula for c - axis resistivity: \[ \hat{R}_c = R_c-\rho_{ab}\cdot\left( \frac{l_{cl}}{w_l\cdot d}+\frac{l_{cu}}{w_u\cdot(d + h)} \right) \] - Measured c - axis resistivity: \[ \rho_c=\frac{\hat{R}_c\cdot A_u}{h} \] - Conductivity correction formula for temperature dependence: \[ \tilde{\sigma}_c(T)=\sigma_c(T)+\langle \theta^2 \rangle\cdot\sigma_{ab}(T) \] These formulas and experimental results together reveal the unique electrical transport characteristics in graphite and provide a new perspective for understanding other layered materials.

Evidence for Disorder Induced Delocalization in Graphite

Fingerprints of Disorder Source in Graphene

Dominant Source Of Disorder In Graphene: Charged Impurities Or Ripples?

Electronic Transport in Disordered Bilayer and Trilayer Graphene

Coexistence of Sharp Quasiparticle Dispersions and Disorder Features in Graphite

Evidence for Weak Antilocalization in Epitaxial Graphene

Low Energy Excitations in Graphite: the Role of Dimensionality and Lattice Defects

Disorder-Induced Delocalization in Magic-Angle Twisted Bilayer Graphene

Magneto-transport in Disordered Graphene: from Weak Localization to Strong Localization

Optical Conductivity Of Disordered Graphene Beyond The Dirac Cone Approximation

Localization and the Kosterlitz-Thouless Transition in Disordered Graphene.

Disorder-induced Enhancement of Transport Through Graphene P-N Junctions

First Direct Observation of Dirac Fermions in Graphite

Metallic-to-insulating transition in disordered graphene monolayers

Non-Ohmic behavior of carrier transport in highly disordered graphene

Signatures of disorder in the minimum conductivity of graphene

Evidence for percolation diffusion of cations and material recovery in disordered pyrochlore from accelerated molecular dynamics simulations

Disorder and Localization of Electrons in Bilayer Graphene

Mesoscopic transport signatures of disorder-induced non-Hermitian phases

Electronic states of disordered grain boundaries in graphene prepared by chemical vapor deposition

Anderson Localization of Electron States in Graphene in Different Types of Disorder