Propagation Mechanism of Brittle Cracks

Itamar Procaccia,Jacques Zylberg
DOI: https://doi.org/10.1103/PhysRevE.87.012801
2012-11-15
Abstract:We employ a recently developed model that allows the study of two-dimensional brittle crack propagation under fixed grip boundary conditions. The crack development highlights the importance of voids which appear ahead of the crack as observed in experiments on the nano-scale. The appearance of these voids is responsible for roughening the crack path on small scales, in agreement with theoretical expectations. With increasing speed of propagation one observes the branching instabilities that were reported in experiments. The simulations allow understanding the phenomena by analyzing the elastic stress field that accompanies the crack dynamics.
Disordered Systems and Neural Networks,Chaotic Dynamics
What problem does this paper attempt to address?
The problem that this paper attempts to solve is about the mechanism of brittle crack propagation in two - dimensional elastic media. Specifically, the researchers explored the following issues through molecular dynamics simulations: 1. **Crack propagation under fixed - clamped boundary conditions**: Traditional molecular dynamics simulations have difficulty achieving brittle crack propagation under fixed - clamped boundary conditions because the crack often decelerates and stops. The researchers attempted to overcome this problem by selecting an appropriate inter - particle potential function and to verify whether self - sustaining brittle crack propagation can be achieved under such settings. 2. **The role of voids in front of the crack tip**: Voids are observed in front of the crack tip in experiments, and these voids have an important impact on the roughening of the crack path. However, this phenomenon is controversial in different experiments. The researchers hope to verify the existence of these voids and their impact on crack propagation through simulations. 3. **Instability when the crack propagation speed increases**: Branching instability is observed when the crack propagation speed increases. The researchers hope to explain this instability through simulations and analyze the physical mechanism behind it. ### Summary of main content - **Model and method**: The researchers used a recently developed model that allows the study of two - dimensional brittle crack propagation under fixed - clamped boundary conditions. They selected an appropriate inter - particle potential function so that the crack can self - sustainably propagate under fixed - clamped conditions. - **Griffith criterion verification**: The consistency between the initial length of the crack and the Griffith criterion was verified through simulations. The Griffith criterion describes the critical length \(L_c\) required for crack growth, which is determined by stress \(\sigma\), elastic modulus \(E\), and surface energy \(\epsilon\): \[ \sigma\sqrt{L_c}=\sqrt{\frac{2E\epsilon}{\pi}} \] - **The role of voids**: The simulation results show that voids do appear in front of the crack tip, and the positions of these voids are random, causing the crack path to become rough on a small scale. The appearance of voids is caused by plastic yielding, which occurs in the region with the maximum pressure, that is, at a certain distance in front of the crack tip. - **Instability**: Branching instability is observed when the crack propagation speed reaches approximately 30% of the Rayleigh wave speed. After two crack tips grow simultaneously for a period of time, competition causes one of the branches to eventually disappear and the other to continue to expand. ### Conclusion The researchers successfully achieved self - sustaining propagation of brittle cracks under fixed - clamped boundary conditions through molecular dynamics simulations, and verified the existence of voids in front of the crack tip and their impact on the roughening of the crack path. In addition, they also observed the branching instability when the crack propagation speed increases. These results provide important theoretical and experimental bases for understanding the propagation mechanism of brittle cracks.