Constitutive behavior of as-cast A356

M. J. Roy,D. M. Maijer,L. Dancoine

DOI: https://doi.org/10.1016/j.msea.2012.03.106

2012-06-10

Abstract:The constitutive behavior of aluminum alloy A356 in the as-cast condition has been characterized using compression tests performed over a wide range of deformation temperatures (30-500°C) and strain rates (\approx0.1-10 /s). This work is intended to support the development of process models for a wide range of conditions including those relevant to casting, forging and machining. The flow stress behavior as a function of temperature and strain rate has been fit to a modified Johnson-Cook and extended Ludwik-Hollomon expression. The data has also been assessed with both the strain-independent Kocks-Mecking and Zener-Hollomon frameworks. The predicted plastic flow stress for each expression are compared. The results indicate that the extended Ludwik-Hollomon is best suited to describe small strain conditions (stage III hardening), while the Kocks-Mecking is best employed for large strain (stage IV). At elevated temperatures, it was found that the Zener-Hollomon model provides the best prediction of flow stress.

Materials Science

What problem does this paper attempt to address?

This paper aims to solve the problem of the constitutive behavior of aluminum alloy A356 in the as - cast condition. Specifically, through a series of compression experiments, the researchers attempted to characterize the flow - stress behavior of this alloy under a wide range of deformation temperatures (30 - 500°C) and strain rates (about 0.1 - 10 s\(^{-1}\)). These experimental results will support the development of various process models including casting, forging and machining.

### Research Background and Problem

Aluminum alloy A356 has gradually replaced iron alloys in transportation applications because it is of great significance in terms of weight reduction and reduction in the number of parts. However, relatively few studies have been conducted on the deformation behavior of A356 alloy in the as - cast state, especially the data under high - temperature and high - strain - rate conditions are very limited. This leads to a lack of sufficient information when optimizing and modeling the pre - casting processing, and these processes will affect the performance of the final components.

### Research Objectives

To fill this gap, the researchers carried out a large number of isothermal compression experiments in order to develop a comprehensive constitutive equation to describe the flow - stress behavior of A356 alloy in the as - cast state. The main objectives of the study are:

1. **Characterize Flow Stress**: Determine the flow stress of A356 alloy at different temperatures and strain rates through experiments.
2. **Model Selection and Comparison**: Evaluate different constitutive models (such as the modified Johnson - Cook model, the extended Ludwik - Hollomon expression, the Kocks - Mecking framework and the Zener - Hollomon model), and compare their performance in predicting flow stress.
3. **Best Model Identification**: Determine the model that is most suitable for describing the flow stress under different thermodynamic states.

### Experimental Methods

The researchers used a thermal - mechanical simulator named Gleeble 13500 to conduct compression experiments. The experimental samples were cylinders with a diameter of 10 mm and a length of 15 mm. The test temperature range was from 30°C to 500°C, and the strain - rate range was from 0.1 s\(^{-1}\) to 10 s\(^{-1}\). Data such as temperature, load, strain and strain rate were recorded during the experiment.

### Results and Discussion

The experimental results show that the flow stress of A356 alloy at different temperatures and strain rates exhibits significant differences. Specifically:

- At low temperatures (< 300°C), the material shows obvious strain hardening and low strain - rate sensitivity.
- Between 300 - 350°C, the strain hardening weakens and the strain - rate sensitivity increases.
- At high temperatures (> 350°C), there is almost no strain hardening, but the strain - rate sensitivity persists.

Through the comparison of different constitutive models, the study found that:

- The extended Ludwik - Hollomon model is most suitable for describing the flow stress under small - strain conditions (third - stage hardening).
- The Kocks - Mecking framework performs best under large - strain conditions (fourth - stage hardening).
- Under high - temperature conditions, the Zener - Hollomon model provides the most accurate flow - stress prediction.

In conclusion, this study, through systematic experiments and model comparisons, provides a detailed characterization and effective prediction tool for the constitutive behavior of A356 alloy in the as - cast state.