Preparation and Properties of High Performance Bismaleimide Resins Based on 1,3,4-Oxadiazole-containing Monomers
Haoyu Tang,Naiheng Song,Zihong Gao,Xiaofang Chen,Xinghe Fan,Qian Xiang,Qifeng Zhou
DOI: https://doi.org/10.1016/j.eurpolymj.2007.01.016
IF: 6
2007-01-01
European Polymer Journal
Abstract:In research towards high performance polymeric materials, two novel series of bismaleimide (BMI) resins based on 1,3,4-oxadiazole-containing monomers have been designed and prepared by the copolymeriziation reaction of 5-tert-butyl-1,3-bis[5-(4-maleimidophenyl)-1,3,4-oxadiazole-2-yl]benzene (Buoxd) or 4,4′-bis[5-(4-maleimidophenyl)-1,3,4-oxadiazole-2-yl]diphenyldimethylsilane (Sioxd) and 4,4′-bismaleimidodiphenylmethane (BMDM) in different feed ratios. The structures, thermal and dynamic mechanical properties of all the resulting BMI resins were carefully characterized by a combination of methods such as IR, DSC, TGA and DMA. Investigation of the copolymerization process has shown that with an increase of the weight ratio of Buoxd or Sioxd, melting transition temperature (Tm) of BMI monomer mixtures decreased and the exothermic polymerization temperature (Tp) increased. For all BMI monomer mixtures, a rapid polymerization process was observed in the early stage, as shown by the IR investigations. No glass transition was observed for the resulting BMI resins in the temperature range from 50°C to 350°C, indicating the formation of highly cross-linking networks. The initial thermal decomposition temperatures (Td) of the BMI resins were in the range of 477–493°C in nitrogen and 442–463°C in the air. Dynamic mechanical analysis (DMA) of the composites made of the BMI resins and glass cloth showed high bending modulus not only at room temperature (E′, 1.9–5.3GPa) but also at high temperature, e.g., 400°C (E′, 1.7–4.4GPa).