Abstract:The 2195 Al-Li alloy, as one of the representative third-generation Al-Li alloys, has extensive applications in lightweight aerospace structures. In this paper, the anisotropy in mechanical properties and microstructure evolution of 2195 Al-Li alloy sheets were investigated under a strain rate of 0.01, 0.1, 1 s-1 and a temperature of 440 and 500 °C. Experimental results showed that the hot tensile properties of the 2195 Al-Li alloy sheet exhibited a strong dependence on loading directions. The peak stress (PS) and elongation (EL) along the rolling direction (RD) were larger than the transverse direction (TD). For the tests carried out at 440 °C-1 s-1, the PS values of the sheets stretched along the RD and TD are 142.9 MPa and 110.2 MPa, respectively. And, most of the PS anisotropy values are larger than 15%. The anisotropy in EL is less significant than in PS. All the differences are about 10%. Moreover, dimples in the samples stretched along RD were more and deeper than those along TD at 440 °C. The fracture morphology along RD and TD were similar, and both were cleavage fractures at 500 °C. Particularly, the fractions of high angle grain boundaries (HAGBs) along TD were all about 5% larger than those of RD. And, there were more small-sized continuous dynamic recrystallization (CDRX) grains inside the initial grains and discontinuous dynamic recrystallization (DDRX) grains featured with the local bulge of grain boundaries along TD. This was due to the smaller average Schmid factor and the vertical EL trend of the initial grains when the samples were stretched along TD. A model of grain evolution during the dynamic recrystallization (DRX) along RD and TD was proposed based on EBSD results. The Schmid factor and banded structure had a more prominent effect on the hot ductility of the 2195 Al-Li alloy compared with the degree of DRX, thus presenting a higher EL and better hot ductility along RD.

Influence of grain orientations on the initiation of fatigue damage in an Al-Li alloy

Anisotropic Low Cycle Behavior of the Extruded 7075 Al Alloy

Effects of grain structures on fatigue crack propagation behavior of an Al-Cu-Li alloy

Microstructural and texture evolution investigation of laser melting deposited TA15 alloy at 500?C using in-situ EBSD tensile test

Effect of grain structure and precipitate on tensile properties and low-cycle fatigue behaviors of 2A55 Al-Cu-Li alloy

The Role of Crystallographic Texture and Basal Plane Slip on Microstructurally Short Fatigue Crack Initiation and Propagation in Forged Billet and Rolled Bar Ti-6Al-4V Alloy

Quantitative analysis of the deformation modes and cracking modes during low-cycle fatigue of a rolled AZ31B magnesium alloy: The influence of texture

The anisotropic fatigue properties of extruded Al–Zn–Mg–Cu alloy

Crack initiation mechanisms of micro-textured Ti60 alloys with different dwell sensitivities subjected to fatigue and dwell fatigue loading

Influence of grain structure and precipitates on fatigue crack propagation behaviors of Al- x Cu-1.2Li-X alloys

Fatigue Behavior of Ultrafine-Grained 5052 Al Alloy Processed Through Different Rolling Methods

Damage Mechanisms and Anisotropy of an AA7010-T7452 Open-Die Forged Alloy: Fatigue Crack Propagation

Quantitative assessment of the microstructural factors controlling the fatigue crack initiation mechanisms in AZ31 Mg alloy

Relationship Between the Fatigue Behavior and Grain Structures of an As-Extruded Mg-6.2%Zn-0.6%Zr (in Wt.%) Alloy

On high‐cycle fatigue anisotropy of an aluminum alloy super‐thick plate

Effect of Initial Orientation on the Anisotropy in Microstructure and Mechanical Properties of 2195 Al-Li Alloy Sheet during Hot Tensile Deformation

In Fl Uence of Texture and Grain Re Fi Nement on the Mechanical Behavior of AA 2219 Fabricated by High Shear Solid State Material Deposition

Influence of Grain Refinement and Microstructure on Fatigue Behavior for Solid-State Additively Manufactured Al-Zn-Mg-Cu Alloy

Small fatigue crack growth in an extruded dual-phase Mg-Li alloy

Mechanism of Precipitate Microstructure Affecting Fatigue Behavior of 7020 Aluminum Alloy

Fatigue crack nucleation and microstructurally small crack growth mechanisms in high strength aluminum alloys