Abstract:The significance of light alloy in realizing the national strategy of energy saving and emission reduction and promoting the upgrading of the manufacturing industry is self-evident. Mg/Al composite laminates combine the lightweight of magnesium alloy and the plasticity and corrosion resistance of aluminum alloy. Traditional accumulative roll bonding technology relies on the advantage of introducing large deformation. Although high strength is obtained, it is often accompanied by a large loss of ductility, and there is a problem that it is difficult to balance strength and ductility. To solve this problem and optimize the process conditions, a new hard-plate accumulative roll bonding process is proposed in this paper, which is used to prepare high-performance Mg/ Al composite plates, and the influence of forming temperature on the microstructure and mechanical properties of Mg matrix is studied. The results show that when the forming temperature is 350 C-degrees, the properties of composite laminates are the best, the tensile strength can reach 243 MPa, the elongation is 14.7 %, and there are a lot of tearing edges and dimples on the fracture surface. At the same time, complete recrystallization can be realized at this temperature, and the opening of non-base slip can coordinate deformation stress, promote the dislocation slip, and reduce the dislocation density, SEM images show that there are no defects such as delamination at the interface, and a firm metallurgical bonding is achieved. It provides a new approach to the forming and manufacturing of high-quality lightweight heterogeneous composite laminates.

Preparation and performance of iron-based amorphous strip/AZ31 Mg alloy laminated composites

Study on Facile Fabrication Method and Performance of Iron-Based Amorphous Alloy/Al Micro-Laminated Composites

Research on the microstructure and properties of iron-based amorphous alloy/Al micro-laminated composites by vacuum hot pressing method

Preliminary Investigations on the Mg–Al–Zn/Al Laminated Composite Fabricated by Equal Channel Angular Extrusion

Microstructure of a Novel Al-based Amorphous Reinforced Aluminum Metal Matrix Composite

Microstructures and Properties of AlMgTi-Based Metal-Intermetallic Laminate Composites by Dual-Steps Vacuum Hot Pressing

Microstructures and mechanical properties of AZ31 magnesium alloys fabricated via vacuum hot-press sintering

Preparation and Properties of Hot-Pressed Al2o3/Al-Steel Mesh-Al Laminated Composites

Microstructure and Mechanical Property Improvement of AZ31B Induced by the Combination of Cold Metal Transfer Welding and Friction Stir Processing

Interfacial characteristics and bending properties of a Ti6Al4V-Mg3AlZn laminate metal composite

Study on the Fine Grain Size and Microhardness at the Interface of AZ31/Mg‐Y Composites

Additive manufacturing of high performance AZ31 magnesium alloy with full equiaxed grains: Microstructure, mechanical property, and electromechanical corrosion performance

Synergistic Mechanism of Strengthening and Toughening of Tissue Regulation Response to Mg/Al Composite Laminates by Hard Plate Accumulative Roll Bonding

Microstructures and Mechanical Properties of Hot Rolled AZ31 Mg Alloy Sheets

Microstructure and Properties of Al Foil Wrapped AZ31 Plate Prepared by Hot Pressing and Annealing

Phase formation and mechanical properties of iron-based intermetallic/steel laminate composites

Study on the Microstructure and Properties of AZ31 Alloy by Hot Die Forging Extrusion

Microstructure and mechanical properties of AZ31 magnesium alloy prepared using wire arc additive manufacturing

Microstructure And Mechanical Properties Of Az31 Magnesium Alloy Sheet By Hot Rolling

Experimental study on properties and structure of magnesium alloy/PC/ABS hybrid materials prepared by hot-press molding technology

Microstructures and Mechanical Properties of Ultrafine-Grained Ti/AZ31 Magnesium Matrix Composite Prepared by Powder Metallurgy