Effects of NaIO4 treatment on the chemical and physical properties of polyacrylonitrile fibers
Hongqiang Zhu,Yatian Chen,Bin He,Qiufei Chen,Hamza Malik,Yuhang Wang,Jian He,Bomou Ma,Xueli Wang,Hui Zhang,Yong Liu
DOI: https://doi.org/10.1080/1023666x.2023.2295630
2024-01-11
International Journal of Polymer Analysis and Characterization
Abstract:Polyacrylonitrile (PAN) fiber modification can promote the stabilization efficiency and mechanical properties of the subsequent carbon fibers; however, it could cause damage to the fibers to some extent. In this article, the effects of NaIO 4 treatment on the chemical and physical properties of PAN fibers were investigated. After NaIO 4 modification, the cyclization reaction has partially occurred, owing to the FTIR revealed that the C≡N peak was weakened, but the C=N stretching vibration peak, the –N = C=O stretching vibration peak, the C=O stretching vibration absorption peak, and the short sequence conjugate C=N characteristic peak were enhanced simultaneously, indicating a successful cyclization and dehydrogenation reaction. Moreover, owing to more oxygen-containing functional groups successfully attached to the PAN fibers and the cyclization reaction taking place, the initial temperature, peak temperature, and heat release of cyclization decreased, which means a more efficient and safer stabilization process. X-ray diffraction (XRD) showed that the (100) crystal plane microcrystal size was the smallest at 40 °C of the modification temperature, whereas the (002) crystal plane microcrystal size was the largest at 60 °C. The modified stabilized PAN fibers presented lower crystallinity and a more aromatic structure compared with untreated fibers. Raman spectra revealed a significant increase in the intensity of the G peak after NaIO 4 modification; the R -value decreased from 1.65 to 1.43, demonstrating a transformation of the sp 3 hybrid carbon structure into a more graphite-like sp 2 hybrid C=C structure. Meanwhile, scanning electron microscopy (SEM) images disclosed additional grooves and cracks on the fiber surface after modification.
polymer science