Structural stability of β-phase uranium films at extreme temperatures

Mengsheng Yang,Taimin Yi,Fengcheng Zheng,Bo Ke,Yong Hu,Ning Li,Pifeng Xing

DOI: https://doi.org/10.1016/j.jnucmat.2022.154210

IF: 3.555

2022-12-25

Journal of Nuclear Materials

Abstract:Pure uranium films have important applications in inertial confinement fusion and X-ray optics, and need to withstand extreme cryogenic temperatures or alternating high–low temperature environments. They are usually prepared via physical vapor deposition and have small grain sizes and metastable phases. Here, the structural stability of uranium films at extreme temperatures was examined. Specifically, nanocrystalline β phase films with a (001) orientation were deposited via magnetron sputtering at 296 K. The phase composition, grain size, and microstrain were characterized with in situ and off-line X-ray diffraction over the temperature range 10 K to 573 K. The orientational correspondence between the parent and product phases in a β–α phase transformation was obtained by two-dimensional X-ray diffraction. Surface morphologies were acquired with white light interferometry. The residual stresses in the films at various temperatures were calculated from the substrate curvature and thermal stress. The β phase and grain size remained constant over the range 10 K to 473 K. At 573 K, a large-scale β–α phase transformation occurred under the combined action of grain growth and compressive stress. Eventually, a strong tensile stress was generated, which inhibited further phase transformations.

materials science, multidisciplinary,nuclear science & technology