Abstract:The liquid state thermophysical properties and amorphous solidification kinetics of Fe50−xCoxCr14Mo14C9B8Tm5 ( x=10 , 15, 20, and 25) alloys were explored by electromagnetic and electrostatic levitation techniques. It was found that the surface tension of liquid alloys with Fe contents below 30 at. % had a strong temperature dependence. The high surface tension led to a sharp increase in the interfacial free-energy penalty. A high nucleation barrier was formed inside the melt, which greatly inhibited the nucleation rate. The liquid viscosity revealed the strong liquid feature of this alloy series, which became the dominant kinetic factor determining their solidification mechanisms. The high viscosity hindered atomic diffusion and delayed nucleation. The long crystallizing incubation time of Fe30Co20Cr14Mo14C9B8Tm5 ensured a strong glass-forming ability and a low critical cooling rate of 2.11×103Ks−1 . As a result, a bulk metallic glass rod with an 8-mm diameter was successfully prepared by a convenient casting procedure. This rod could remain in a glassy state at a higher temperature and over a wider temperature range due to its high glass-transition temperature and large undercooled liquid region. The apparent activation energy for nucleation was derived as 463.8 kJmol−1 according to the nonisothermal crystallization kinetics, indicating that the bulk metallic glass had to absorb a large amount of energy to overcome the potential barriers before nucleation and thus exhibited excellent thermal stability. https://doi.org/10.1103/PhysRevE.110.034612 ©2024 American Physical Society

Compaction of bulk amorphous Fe40Ni40P14B6 alloys

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Crystallization of Bulk Amorphous Alloy (Fe40ni40p14b6)(96)ga-4 in Supercooled Liquid Region

Synthesis of Highly Amorphous Fe 70 Ti 2 Y 6 B 22 Bulk Alloy with Excellent Thermal Stability by Isothermal Compression under High Pressure

PREPARATION AND PROPERTIES OF BULK AMORPHOUS Fe-Ni-P-B-Ga ALLOYS

Cold Compaction Behavior of Nano-Structured Nd–Fe–B Alloy Powders Prepared by Different Processes

Full-density nanocrystalline Fe-29Al-2Cr intermetallic consolidated from mechanically milled powders

Nanocrystalline Structures of Fe-Ni-P-B Alloy Solidified at Large Undercooling and Liquid Spinonal Decomposition

Formation of ferromagnetic bulk amorphous Fe40Ni40P14B6 alloys

The Microstructure Evolution of a Fe-Ni-P-B Soft Magnetic Alloy Solidified at Different Undercooling

Formation of bulk ferromagnetic nanostructured Fe40Ni40P14B6 alloys by metastable liquid spinodal decomposition

Solidification Structure Formation in Undercooled Fe–Ni Alloy

Nanophase Metallic Alloys Consolidated from Powders Prepared by Mechanical Alloying

Cold Densification Behaviour of Multiple Alloy Powder Containing Fe–Cr and Fe–Mo Hard Particles

Nanophase Fe Alloys Consolidated to Full Density from Mechanically Milled Powders

Research on the Densification Process of the Mechanically-Alloyed Amorphous 2Si-B-3c-n Powder

Liquid state properties and amorphous solidification kinetics of multicomponent alloys investigated under containerless processing conditions

Solidification structure of undercooled Ni54.6Pd45.4 alloy

Liquid state properties and amorphous solidification kinetics of multicomponent Fe_{50-x}Co_{x}Cr_{14}Mo_{14}C_{9}B_{8}Tm_{5} alloys investigated under containerless processing conditions

Structural Changes Caused by High-Temperature Holding of Powder Shape Memory Alloy 66% Fe – 14% Mn – 6% Si – 9% Cr – 5% Ni

Phase transformation and thermal stability of mechanically alloyed W–Ni–Fe composite materials