LI Gaohui,ZHOU Li,Haifeng ZHANG,LUO Sanfeng,GUO Ning,Gaohui LI,Li ZHOU,Sanfeng LUO,Ning GUO

DOI: https://doi.org/10.1016/j.cja.2020.05.037

IF: 5.7

2021-12-01

Chinese Journal of Aeronautics

Abstract:Evolutions of grain structure, texture and mechanical properties in ZK60 Mg alloy occasioned by bobbin tool FSW were measured.Dispersion and segregation of Zr-rich precipitates occurs in the stir zone (SZ), which results in evolution of a bimodal grain structure.Texture distribution of the BTFSW joint exhibited different characteristics with respect to that of the FSW joint.The overall variation trend of hardness of the joint exhibited weak grain size dependence.Texture distribution is the dominate factor affecting the fracture behavior of the BTFSW joint.ZK60B (Mg-6% Zn-0.6% Zr) alloy joints fabricated by bobbin tool friction stir welding (BTFSW) with various traverse speeds were investigated. The sound joint fabricated by the BTFSW was possible under the appropriate welding parameters. The severe plastic deformation during BTFSW resulted in dispersion and segregation of the Zr-rich particles within the stirred zone (SZ) followed by evolution of a bimodal grain structure with distributed bands of 0.8-1.7 μm ultrafine grains and 4.1-7.1 μm equiaxed grains. Micro-hardness of SZ is substantially reduced in contrast to that of parent metal (PM) in spite of the finer grain size owing to dissolution of Mg-Zn based precipitates having hardening effects on alpha-Mg matrix. With the decrease in traverse speed, randomization degree of the plasticized metal flow increases, which is evidenced by the randomized arc line pattern at the low traverse speed. Among all defect-free joints, the 200 mm/min joint exhibits the weakest isotropy of texture within SZ and the best tensile properties, which has reduced ultimate tensile strength and yield strength by 5.4% and by 22.2%, respectively, as compared to the PM. The randomized texture hinders the joint fracturing within SZ at low elongation. Therefore, a relatively high elongation of 10.8% was achieved, which corresponded to 72% of the PM value.

engineering, aerospace