Abstract:<p>Poly(lactic acid), a promising biodegradable polymer, is restricted by poor heat resistance, which is determined by the crystallization. It is important to expound the relationship between crystal structure and thermal, mechanical performance. Several PLA specimens were prepared by fully crystallized at different temperature (100 ºC, 110 ºC, 115 ºC, 120 ºC, and 130 ºC) from melt state. The morphology, crystallization behaviors, thermal and mechanical properties were evaluated by polarizing optical microscope (POM), wide-angle X-ray diffraction (WAXD), differential scanning calorimeter (DSC), dynamic mechanical analysis (DMA), and Vicat softening temperature (VST), respectively. It was found that the PLA crystal shows the characterization of spherulite and many nuclei are generated at low temperature (100 ºC and 110 ºC). The nuclei gradually decrease and the spherulites grow as the crystallization temperature increases. Compared with the amorphous PLA specimens, the tensile strength of crystallized samples gradually decreases from 29.4 MPa to 25.8 MPa and the VST is improved from 51.6 ºC to 64.9 ºC. It confirms that the crystallization is an effective way to enhance the heat resistance. However, when the temperature reaches 130 ºC, the crystalline and amorphous region aggregate, forming the distinct two phases, which leads to a decrease in VST (53.2 ºC). Meanwhile, the spherulites become irregular, larger, and imperfect at high temperature, resulting in the further deterioration of mechanical performance. In addition, the molecular dynamics was further used to simulate the structural evolution during the crystallization and reveals the mechanism behind the relationship.</p>

Effect of poly (lactic acid) crystallization on its mechanical and heat resistance performances

Effect of poly(lactic acid) crystallization on its mechanical and heat resistance performances

Effect of Crystallization Temperature on Crystal Modifications and Crystallization Kinetics of Poly(l‐lactide)

Crystallization Behavior and Water Vapor Permeability of Poly(Lactic Acid) Nanocomposite under Oscillatory Shear

Polymorphous Crystallization And Multiple Melting Behavior Of Poly(L-Lactide): Molecular Weight Dependence

Crystallization Morphology Regulation on Enhancing Heat Resistance of Polylactic Acid

Thermal Strain-Induced Cold Crystallization of Amorphous Poly(lactic Acid)

Influence of Non-Isothermal Melt Crystallization on the Thermal Behavior and Morphology of Poly-L-Lactide

Dynamics Affected Memory for Crystallization Behaviors of Poly (D-Lactic Acid)

The Preparation of Crystalline and Heat Resistance PLA in the Presence of Fully Biodegradable Macromolecular Nucleating Agent

Tailoring the Thermal and Mechanical Properties of Injection‐molded Poly (lactic Acid) Parts Through Annealing

Effects of thermal treatment on the microstructure and thermal and mechanical properties of poly(lactic acid) fibers

Thermal And Crystallinity Property Studies Of Poly (L-Lactic Acid) Blended With Oligomers Of 3-Hydroxybutyrate Or Dendrimers Of Hvdroxyalkanoic Acids

Preparation and properties of the crosslinked poly( L -lactide) with high crystallinity and high gel content

Tailoring the Melt Viscoelasticity and Crystallization Behavior of Poly(lactic acid) during Processing

Temperature Dependence of Poly(Lactic Acid) Mechanical Properties

Enhancing Thermomechanical Properties and Heat Distortion Resistance of Poly( l -lactide) with High Crystallinity under High Cooling Rate

Effect of crystallization on enhancement of mechanical property for polylactide-<i>b</i>-polyisoprene-<i>b</i>-polylactide triblock copolymers

Highly Crystallized Poly (lactic Acid) under High Pressure

Toughening of Poly(L-Lactic Acid) by Annealing: the Effect of Crystal Morphologies and Modifications

Highly Toughened and Heat-Resistant Poly(lactic acid) with Balanced Strength Using an Unsaturated Liquid Crystalline Polyester via Dynamic Vulcanization