Abstract:This study reports the synthesis of Ni-Co-SiC coatings onto Q235A steel substrates through magnetic-field-induced electrodeposition to improve the surface performances of the machine parts. The microstructure, topology, roughness, corrosion, and wear resistances of the coatings were investigated through X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), atomic force microscopy (AFM), hardness testing, electrochemical analysis, and friction wear testing, respectively. The Ni-Co-SiC coating deposited at 0.4 T (MS1) with a perpendicular magnetic direction showed the maximum SiC content and NiCo grain size (86.5 nm). The surface topology was also fine, dense, and smooth. In addition to that, the images obtained from the AFM characterization showed that the surface roughness of the MS1 coating was 76 nm, which was significantly lower compared to the roughness observed in Ni-Co-SiC coatings fabricated under the magnetic induction of 0 T (MS0) and magnetic field applied in a parallel direction to 0.4 T (MS2). The XRD results revealed that the preferential growth direction of the NiCo grains was changed from the (200) crystal plane to the (111) plane with the introduction of a perpendicular magnetic field. Moreover, MS2, MS1, and MS0 had thickness values of 25.3, 26.7, and 26.3 μm, respectively. Among all the coatings, MS1 showed the lowest friction coefficient and the highest hardness value (914.8 HV), suggesting enhanced wear resistance. Moreover, the MS1 coating revealed a maximum corrosion potential of −257 mV, and the lowest corrosion current of 0.487 μA/cm2, suggesting its improved corrosion resistance.

Fabrication and characterization of C3N4 coating by electrochemical deposition on stainless steel

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Microstructure and Tribological Properties of Multilayered ZrCrW(C)N Coatings Fabricated by Cathodic Vacuum-Arc Deposition

Nitrogen diffusion mechanism, microstructure and mechanical properties of thick Cr/CrN multilayer prepared by arc deposition system

Microstructure, Adhesion and Tribological Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrocarburized AISI 4140 Steel

Tribological and electrochemical properties of Cr–Si–C–N coatings in artificial seawater

Effect of C doping on structure and properties of TiAlCrN coatings by filter cathode vacuum arc deposition

Microstructure, mechanical properties and tribo-corrosion mechanism of (CrNbTiAlVMo) x N 1-x coated 316 L stainless steel in 3.5 wt.% NaCl solution

Microstructure, Mechanical and Adhesive Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrided AISI 4140 Steel

Influence of Electrodeposition Process Parameters and Si3N4 Nanoparticle Concentration on Microhardness and Wettability of Ni-Co-Si3N4 Nanocomposite Coatings

Investigation of the anti-corrosion performance of a Cu/Ni–B4C superhydrophobic coating with self-cleaning and abrasion resistance properties

Preparation and Corrosion Resistance of Ni-W-CF Composite Coating on P110 Steel

Corrosion and tribocorrosion behaviors of ternary TiZrN coating on 304 stainless steel prepared by HiPIMS

Electrochemical Behavior of (cr, W, Al, Ti, Si)N Multilayer Coating on Nitrided AISI 316L Steel in Natural Seawater

Preparation and Performance of a Cr/CrN/TiAlCN Composite Coating on a GCr15 Bearing Steel Surface

Study on superhydrophobicity and excellent corrosion resistance of a novel Ni‐SiC nanocomposite coating

Microstructure and Electrochemical Characterization of Ti–Al–C–N Coatings As Biological Dry Electrodes

Impact of Magnetic Field Direction on Performance and Structure of Ni-Co-SiC Coatings Fabricated via Magnetic-Field-Induced Electrodeposition

Structure, corrosion, and tribological properties of CrSiN coatings with various Si contents in 3.5% NaCl solution

Microstructure, Mechanical Properties, and Oxidation Resistance of Nanocomposite Ti–Si–N Coatings